Electronics Forum | Wed Aug 21 17:43:12 EDT 2002 | davef
Your flux supplier will have good suggestions.
Electronics Forum | Wed Aug 21 10:20:05 EDT 2002 | ksfacinelli
Dave, I am interested in a amine hydrochloride activated flux. Can you give suggestions on readily available fluxes that you have used that have strong deoxidization properties. I am looking at something that could be used in a pinch when the stan
Electronics Forum | Tue Aug 20 18:15:02 EDT 2002 | davef
Haaaaa!!!! Soldering to plastic!!!! An apt analogy!!! I like to compare it to soldering to dirt. Some thing. In fact, you are soldering on nickel, when soldering on many things. It�s just that the gold, er Pd, flash enables the wetting mechanism
Electronics Forum | Mon Jan 08 03:16:12 EST 2007 | oswald5087
hi' i need advise on immersion gold PCb shelf life. 1) what is the issue shelf life or expire for Immersion gold PCB? 2) How long we can keep the PCB? (with vacuum seal and without vacuum seal) 2) iF PCB expire, can we bake the immersion PCB? what t
Electronics Forum | Wed Jul 29 13:44:45 EDT 1998 | David Spilker
We are investigating alternatives to HASL finishes for more dense PWBs. OSP is not a good choice because of low solid flux and possibly long shelf life. Immersion gold is expensive and so far has been more difficult to wave solder. Has anyone had
Electronics Forum | Mon Jan 08 17:32:47 EST 2007 | Board House
Hi Oswald, Shelf life with ENIG if vacuum sealed and kept in controled enviroment would be 12 to 14 months. Shelf life in shrink wrap - No recomended packaging, 6 moths. If Shelf life goes over the 12 -14 months - Baking ? I would not suggest re-b
Electronics Forum | Tue Nov 05 09:57:45 EST 2013 | cuperpeter
Hello All, We have a problem with dewetting of solder paste. Problem is most visible on the pads without components (see attached pictures) and occurs randomly, 20% of PCB's. Pcb supplier sent us a cross-section of pads with thickness of Cu, Ni and
Electronics Forum | Wed Nov 06 03:51:28 EST 2013 | cuperpeter
Hi rob, Thank you very much for your response. Profiling was made exactly on the pad, which showed dewetting, so the values are mentioned for this pad. PCB's is about a week old. It is possible that the surface of pads is already oxidized? I will t
Electronics Forum | Thu May 10 18:23:50 EDT 2007 | wayne123
I was just wanting to know some of the advantages/disadvantages of going gold immersion? Is this neccessary for Lead free?
Electronics Forum | Fri May 18 15:41:40 EDT 2007 | wayne123
thanks for the input Rob, I apprieciate the help