Technical Library | 2019-06-12 10:33:58.0
The success of ball grid array (BGA) placement on electronic assemblies is as much a matter of proper preparation and planning, as it is technique. In some designs, it is more appropriate to apply BGAs using a rework station that isolates the placement of the device, without subjecting the entire assembly to thermal reflow. This is especially beneficial in board constructions where the number of BGAs is limited, and the application of the solder paste is difficult, due to small pitch features that stretch the limitation of the stencil construction. Another application for rework stations, involves very large and thermally conductive BGAs, which will not uniformly reflow with other components on the assembly, and may require special process parameters for their proper placement. The most common use of BGA rework stations are for assemblies requiring BGA removal and replacements due to failures in the initial assembly stage.
Technical Library | 2019-09-23 09:35:00.0
Failure analysis (FA), by its very nature, is needed only when things goawry. Before any testing is performed on the sample, a decision mustbe made as to whether or not the sample is allowed to be destroyedin the process of testing. Non-destructive testing can allow for re-use of the assembly since the functionality is not altered, but there still remains the possibility that inadvertent damage can occur through the course of the analysis. If non-destructive testing is preferred, then the following types of analysis can be performed. The testing can be divided into four categories: visual, X-ray (X-ray imaging and X-ray fluorescence), cleanliness (resistivity of solvent extract, ion chromatography, and Fourier transform infrared spectroscopy), and mechanical (non-destructive wire bond pull).
Technical Library | 2020-05-08 18:22:31.0
A customer contacted the Helpline to perform analysis on a lead-free assembly which exhibited intermittent functionality. The lead-free assembly exhibiting intermittent functionality when pressure was applied to the ball grid array (BGA) packages. Industrial adaptation of a Restriction of Hazardous Substances (RoHS) compliant solder standard has created a new host of failure modes observed in lead-free assemblies. Pad cratering occurs when fractures propagate along the epoxy resin layer on the underside of the BGA connecting pads. While originating from process, design, and end use conditions, it is the combination of a rigid lead-free solder with inflexible printed circuit board (PCB) laminates that has advanced the prevalence of this condition. Pad cratering is simply the result of mechanical stress exceeding material limitations.
Technical Library | 2020-11-09 16:59:53.0
A customer contacted ACI Technologies regarding a high failure rate of their assemblies. They provided assemblies to be X-rayed and inspected for the purpose of identifying any process related issues such as (but not limited to) solder and assembly workmanship and evidence of damage due to moisture related problems during reflow (a.k.a. "popcorning"). Moisture damage usually appears as physical damage to the component. The first indication of moisture damage would be externally observable changes to the package in the form of bulging or fractures to the outer surface of the component, an example of which is shown in Figure 1. Internally observable indicators of moisture damage typically include fractures to the die inside the package and lifted or fractured wire bonds. These conditions would be apparent during transmissive X-ray inspection. Another symptom of moisture related damage would be inconsistent solder joint sizes that result from package deformation during the liquidus phase of the reflow process. None of these indicators of moisture related damage were present on the customer samples.
Technical Library | 2010-01-13 12:34:10.0
Micro-sectioning (sometimes referred to as cross-sectioning)is a technique, used to characterize materials or to perform a failure mode analysis, for exposing an internal section of a PCB or package. Destructive in nature, cross-sectioning requires encapsulation of the specimen in order to provide support, stability, and protection. Failures that can be investigated through micro-sectional analysis include component defects, thermo-mechanical failures, processing failures related to solder reflow, opens or shorts, voiding and raw material evaluations.
Technical Library | 2021-03-10 23:57:29.0
Latent short circuit failures have been observed during testing of Printed Circuit Boards (PCB) for power distribution of spacecraft of the European Space Agency. Root cause analysis indicates that foreign fibers may have contaminated the PCB laminate. These fibers can provide a pathway for electromigration if they bridge the clearance between nets of different potential in the presence of humidity attracted by the hygroscopic laminate resin. PCB manufacturers report poor yield caused by contamination embedded in laminate. Inspections show ...
Technical Library | 2010-10-13 17:29:21.0
The number of failures caused by electrostatic discharges (ESD) has been increasing for some time now. So, it is necessary for everyone, who handles electrostatic sensitive devices (ESDS), to know the reasons of such failures. This presentation will give
Technical Library | 2009-04-30 18:06:24.0
This presentation surveys the most significant via and via-related laminate failure mechanisms from past to present using data from current induced thermal cycling (CITC) testing, failure analysis, and other sources. The relative life and failure modes of thru vias, buried vias, and microvias (stacked vs. non-stacked) are compared, along with the affect of structure, materials, and peak temperatures on the above. The origin of via-induced laminate failures such as "eyebrow cracks" and Pb free related internal delamination is also explored.
Technical Library | 2022-12-05 16:22:13.0
This paper reviews the possible causes and effects for no-fault-found observations and intermittent fail- ures in electronic products and summarizes them into cause and effect diagrams. Several types of inter- mittent hardware failures of electronic assemblies are investigated, and their characteristics and mechanisms are explored. One solder joint intermittent failure case study is presented. The paper then discusses when no-fault-found observations should be considered as failures. Guidelines for assessment of intermittent failures are then provided in the discussion and conclusions.
Technical Library | 2021-07-27 14:49:16.0
Conductive anodic filament (CAF) formation, a failure mode in printed wiring boards (PWBs) that are exposed to high humidity and voltage gradients, has caused catastrophic field failures. CAF is an electrochemical migration failure mechanism in PWBs. In this article, we discuss CAF, the factors that enhance it, and the necessary conditions for its occurrence. Published studies are discussed, and the results of historical mean time to failure models are summarized. Potential reasons for CAF enhancement solutions are discussed, and possible directions in which to develop anti-CAF materials are proposed.