Electronics Forum | Tue Apr 13 21:33:48 EDT 2004 | qualitel
Hi Dreamsniper, It seen this is the major issue had been occurs you.( We had face all this issue last time too) We had done a lot of areospace products before and most of ours products is a must on class 3 spec. BGA is not that tough t
Electronics Forum | Tue Dec 14 18:03:22 EST 2004 | Dreamsniper
Hi, Can you guide with the above? I read ROSE Test is a process control tool. What about Ion Chromatography, SIR and FT-IR. What Accpetance Criteria will I use for our assembly when using WS Flux? My WS Flus says it has 0% Halide so What can Ion Chr
Electronics Forum | Thu Dec 23 03:13:47 EST 2004 | Steve Stach
The "Rose" test is a process control tool because it is cheap and easy to use. It has it's problems; but, it is generally agreed to be the best tool available for this purpose. All others are much more expensive and time consuming to run every day.
Electronics Forum | Thu Oct 05 16:04:00 EDT 2006 | GS
I am not expert, just my comment, the total ionic contamination allowed after SMT, by using No Clean process, theoretically it should be close to Zero. Any way the Standard IPC-JSTD-001 allows 1,56 ugr NaCl/cm2 for the final Printed Board assembled.
Electronics Forum | Mon Apr 19 10:52:05 EDT 2010 | esca
Hi, if you want to verify the gold contamination, is mandatory to use the XPS and FTIR analysis, but is difficult think about a gold contamination from 3 different manufacturers. Do you have cleaned the PCBs after an erroneous screen process ? If no
Electronics Forum | Fri Jun 07 11:39:33 EDT 2019 | gregoryyork
I feared so. The only thing to be done is to tell the PCB manufacturer to increase the Thermal cure so dont set the oven to 150C but to 170C and actually measure the middle board and once it hits 155C then give it an hour cure from then. Also insist
Electronics Forum | Tue Apr 17 09:38:04 EDT 2001 | CAL
With some help from our good Friends at Agilent Technologies our RF Lab includes testing up to 100GHz. Equipment includes Vector network analyzer, signal analyzer, dual channel power meter, noise filter meter, advanced impedance analyzer (including
Electronics Forum | Tue Jun 02 14:32:58 EDT 1998 | Chris Fontaine
We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not alwa
Electronics Forum | Tue Jun 02 15:53:32 EDT 1998 | Earl Moon
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Wed Jun 03 07:13:27 EDT 1998 | Tom Tellinghuisen
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al