Electronics Forum | Thu Dec 17 18:24:37 EST 2020 | SMTA-64387520
We use both in our selective soldering machine. Training is the most important concern. As long as you have well trained operators the risk is minimized.
Electronics Forum | Wed Jan 20 07:11:01 EST 2021 | janwillemreusink
Thanks for replying... Unfortunately (or not) it isn't relevant anymore. Due to the effects of covid-19 we don't have any active aerospace customers anymore so (for now) we're only making leadfree products.
Electronics Forum | Tue Dec 15 14:38:23 EST 2020 | emeto
I have done it different ways on different equipment. 1. Remove alloy one from the machine. Add alloy two only. and use it.For next board, do the same. 2. There are machines with separate sections for PB and PC-Free, so pots are away from each other
Electronics Forum | Thu Dec 10 12:12:40 EST 2020 | robl
Yep, done it previously with a multipot machine. Using with wirefeed to top up the pots means you only have a contamintion risk when you fit a new top up reel. Used separate nozzles for both, but theoretically using titanium nozzles would mean no c
Electronics Forum | Fri Jul 06 12:11:34 EDT 2007 | james
We are starting to see issues with using Kester WS R562 with lead free components. The joints look grainy on almost all of the 0402'2 and other small components. Some of the solder does not solder to the terminations. These are hybrid boards which
Electronics Forum | Fri Jul 06 12:39:01 EDT 2007 | blnorman
What's the metallization on the board? We use an immersion tin board and had to increase our profile to successfully solder.
Electronics Forum | Fri Jul 06 13:44:15 EDT 2007 | shrek
Krikies! seems like a head-scratcher if I may say so me-self. I would say the other ogre is right, that surface finish will play a big factor in your solder joint's grain structure or how shiney 'tis. Non-HASL bearing finishes will typicaly exhibit
Electronics Forum | Wed Apr 26 01:18:33 EDT 2006 | ge_lim
Hi We are in the process of developing a lead free product to be used in a non lead free selective soldering machine, i do have concern in these, and hope you guy can share your experienced expert opinion: 1. What does it take to convert to lead fre
Electronics Forum | Wed Apr 26 07:37:34 EDT 2006 | amol_kane
"Can we reuse the same machine? My point here is that the non lead free process has already coated the machine interior ( exhaust, internal flow ) with leaded component, and by conversion to lead free are we containminating the lead free product from
Electronics Forum | Wed Apr 26 07:37:52 EDT 2006 | amol_kane
"Can we reuse the same machine? My point here is that the non lead free process has already coated the machine interior ( exhaust, internal flow ) with leaded component, and by conversion to lead free are we containminating the lead free product from