Electronics Forum | Tue Dec 05 15:10:55 EST 2000 | Francois Monette
Victor, here are a few more elements of information to answer your question. Both the temperature and relative humidity on the manufacturing floor have a significant impact relative to the rate of diffusion of moisture inside a plastic package and t
Electronics Forum | Mon Jun 08 15:29:17 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Mon Jun 08 14:52:16 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Thu Sep 04 03:26:18 EDT 2014 | eurekadrytech
Hi all: Interesting question you have raised as it concerns the rate of absorption by the board material. I represent http://www.EurekaDrytech.com and could assist in resolving the blistering problems you're facing. First some questions. 1. Is the
Electronics Forum | Thu Jun 24 11:41:10 EDT 1999 | John Thorup
| Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody hel
Electronics Forum | Mon Aug 18 15:04:25 EDT 2014 | rgduval
Off hand, I can't recall a "formula" for how long boards could sit in a specific RH environment. I've done a couple of quick Google searches, and can find a bunch of information on the dispersion rate of moisture in various PCB materials, but, nothi
Electronics Forum | Thu Jun 24 12:43:08 EDT 1999 | Earl Moon
| | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody h
Electronics Forum | Sun Sep 07 20:51:52 EDT 2014 | natashakt
1. Is the high RH environment consistently at 72% RH and 21.4 degrees Celsius? No, over the past 2 weeks I have recorded the highest at the moment: 67% RH at 22.6 degrees C and lowest (it is Spring not summer yet): 31.9% RH at 19.0 degrees C. Or d
Electronics Forum | Fri Jun 25 01:11:31 EDT 1999 | Vinesh Gandhi
| | | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody
Electronics Forum | Wed Jan 06 04:51:16 EST 1999 | Earl Moon
| | A question for you all! | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we could not clea