Electronics Forum | Tue Aug 17 10:41:13 EDT 1999 | Steve A
Wayne, Sounds like a gasketing problem. When the horizontal apertures are bleeding but not the vertical apertures. Could be poor underside support, HASL miniscus issues, masking or plugging issues, but what many people do not account for is that t
Electronics Forum | Tue Sep 14 14:07:45 EDT 2010 | grahamcooper22
Hi Gani, HASL is normally very good for solderability providing there is a good consistent coating of HASL on the pcb pad. But it is not unusual to have a very thin coating of HASL on the pad and this is poor for solderability. You then have tin/copp
Electronics Forum | Thu Aug 31 18:59:55 EDT 2000 | Brian W.
Our customers use OSP, HASL, immersion tin and immersion gold as board finishes. If I recommend a finish to the customer, it is one of the immersion finishes or OSP. Those finishes have the advantage of a flat surface to deposit paste. HASL has va
Electronics Forum | Tue May 09 22:57:58 EDT 2006 | davef
The NexLev connector is built in a stripline construction, providing a continuous ground plane for each signal contact. The connectors come as tenrow connectors with 100, 200, or 300 positions at possible stacking heights from 10 mm to 30 mm. Technic
Electronics Forum | Tue May 31 10:44:16 EDT 2005 | Scott B
We have found that when the HASL thickness is less than 5 microns the tin in the HASL reacts with the copper leaving a SnCu surface with poor solderability and microscopic grainy Pb islands. The IPC does not specify minimum HASL thickness but we now
Electronics Forum | Thu Apr 16 13:50:49 EDT 1998 | Lou
| We are having some difficulty soldering a 240 pin Altera device. We use Alpha WS-609, a very generic profile for that solder paste, and a 6 mil stencil with laser cut apertures (1:1 ratio). This is a 20 mil pitch device (aperture size is 10 mils X
Electronics Forum | Thu Apr 16 13:47:36 EDT 1998 | Lou
| We are having some difficulty soldering a 240 pin Altera device. We use Alpha WS-609, a very generic profile for that solder paste, and a 6 mil stencil with laser cut apertures (1:1 ratio). This is a 20 mil pitch device (aperture size is 10 mils X
Electronics Forum | Sun Nov 24 09:54:24 EST 2002 | davef
On a HASL board that has poor wetting on the pad, consider looking further downstream in the process than your assembly shop. For instance, take a look at the bare boards. Look for solder mask bleed onto the pads. This will show-up on the outside
Electronics Forum | Fri Jun 07 05:08:08 EDT 2019 | gregoryyork
Does look like delam, if its that bad and the board looks like its HASL finish or Silver, it could also be porous absorbing the chemistries of HASL or Nitric from the Silver which will greatly encourage ECM or poor SIR figures or just simply eat the
Electronics Forum | Thu Feb 10 04:37:29 EST 2000 | Wolfgang Busko
Russ: If it�s true that they have been reworked to HASL I guess that something went awefully wrong at that stage. If you have some bareboards left have them checked thoroughly. M2C Wolfgang