Electronics Forum | Tue Aug 28 11:12:23 EDT 2007 | grics
This is what I was thinking, but I am being beat up pretty badly by the selective solder. Ambient temperature is anywhere in the the neighborhood of 76 - 80 degrees F. I am not sure of the RH, but I wouldn't think that would be my issue... One of
Electronics Forum | Thu Sep 15 08:39:10 EDT 2016 | davef
J-STD-001 Revision F with Amendment 1
Electronics Forum | Fri Aug 24 11:03:15 EDT 2007 | hussman
I agree with Joris. But to add to his comment, the type of finish also has a direct affect to your wave solder process. Going from a gloss finish to a matte finish may help a lot. As for humidity affecting your wave - I doubt it. I use a water
Electronics Forum | Tue Jun 29 13:52:32 EDT 2004 | microniks
Where to find detailed information on fluxes? No one seems to know the real difference between Rosin fluxes with colophan, Resin fluxes or synthetic Resin fluxes, No Clean, Low Residues, VOC-Free, Halide-Free, Water Washable with alcohol base, Resin-
Electronics Forum | Tue Jun 29 13:56:27 EDT 2004 | Pierre
Where to find detailed information on fluxes? No one seems to know the real difference between Rosin fluxes with colophan, Resin fluxes or synthetic Resin fluxes, No Clean, Low Residues, VOC-Free, Halide-Free, Water Washable with alcohol base, Resin-
Electronics Forum | Fri Sep 26 12:57:09 EDT 2003 | Angie
We have had some components that popped off in our IR oven. It was attributed to the solder paste. The humidity was above 60% the temp was about 70 degrees.
Electronics Forum | Fri Aug 24 09:29:08 EDT 2007 | jgrootkoerkamp
Solder balls with wave soldering can have different causes. The two most important are the solderresist and the flux. I have similar problems, after changes the flux type 90% off all solderballs are gone. KR, Joris Groot koerkamp
Electronics Forum | Fri Aug 24 12:39:59 EDT 2007 | hussman
I would say no, unless your machine is in extremeconditions. You may want to check your flux / preheat out as well. If you are leaving a lot of flux on the board at wave, it may be boiling - which can cause solder balls.
Electronics Forum | Thu Feb 22 21:01:12 EST 2001 | davef
We don't do this, but if we had to and lacking better advice, for all components I�d dry pack according to J-STD-033, store in a low temperature and humidity controlled environment [maybe using some semicon fab inert storage cabinets], review the eff
Electronics Forum | Mon Jul 29 11:28:09 EDT 2002 | yngwie
Is there a difference between the Nitrogen cabinet vs Dry cabinet ? How does this helps in creating safe environment for MSD storage. I felt puzzled when my customer rejected me coz' I'm using the Nitrogen cabinet instead of dry cabinet. Except for t