Testing Printed Circuit Boards for Creep Corrosion in Flowers of Sulfur Chamber

Technical Library | 2015-07-16 17:24:23.0

Qualification of electronic hardware from a corrosion resistance standpoint has traditionally relied on stressing the hardware in a variety of environments. Before the development of tests based on mixed flowing gas (MFG), hardware was typically exposed to temperature-humidity cycling. In the pre-1980s era, component feature sizes were relatively large. Corrosion, while it did occur, did not in general degrade reliability. There were rare instances of the data center environments releasing corrosive gases and corroding hardware. One that got a lot of publicity was the corrosion by sulfur-bearing gases given off by data center carpeting. More often, corrosion was due to corrosive flux residues left on as-manufactured printed circuit boards (PCBs) that led to ion migration induced electrical shorting. Ion migration induced failures also occurred inside the PCBs due to poor laminate quality and moisture trapped in the laminate layers.

iNEMI (International Electronics Manufacturing Initiative)

THERMOCONDUCTING SILICONE PASTE H

THERMOCONDUCTING SILICONE PASTE H

New Equipment |  

facilitates the flow of heat between electronic elements and their radiators, necessary for proper functioning of all kinds of temperature sensors, protects against weather factors, prevents from breakdowns, features a very good chemical resistance t

AG Termopasty

New Yorker Electronics Releases New Innodisk Anti-Sulfuration DRAM Modules

Industry News | 2021-09-10 11:17:18.0

Next Generation of 16GB & 32GB Industrial-Grade Innodisk JESD79-5 DDR5 SDRAM Offer improvements in Capacity, Speed and Voltage

New Yorker Electronics

Monitoring of chlor-alkali electrolysis sub-processes

Industry News | 2022-03-25 08:07:42.0

Easily monitor process fluids in real time with LiquiSonic®

SensoTech Inc.

Which is Better with New Energy Vehicle Lead-acid Battery or Lithium Battery?

Industry News | 2020-12-04 01:59:46.0

Currently, new energy vehicles use lithium batteries as power batteries.

Guangdong Bell Experiment Equipment Co.,Ltd

Corrosion Testing For Electronic Equipment

Events Calendar | Tue Feb 18 00:00:00 EST 2020 - Tue Feb 18 00:00:00 EST 2020 | ,

Corrosion Testing For Electronic Equipment

CALCE Center for Advanced Life Cycle Engineering

Creep Corrosion Of Electronic Assemblies In Harsh Environments

Technical Library | 2022-03-16 19:41:17.0

Creep corrosion occurs in electronics assemblies and it is reminiscent to electromigration but does not require electrical field to drive the reaction. Corrosive elements and moisture must be present for creep corrosion to occur. Sulfur is the most prominent element to cause creep corrosion in environments such as paper mills, rubber manufacturing, mining, cement manufacturing, waste water treatment etc., also including companies and locations nearby such industries. The main part of printed circuit board assembly (PCBA) to be affected is the PCB surface finish. Especially immersion silver is prone to creep corrosion, but it sometimes occurs in NiPd (lead frames), and to a lesser extent in ENIG and OSP surface finishes. As the use of immersion silver is increasing as PCB surface finish and electronics are more and more used in harsh environments, creep corrosion is a growing risk. In this paper we will present the driving forces and mechanisms as well as suitable tests and mitigation strategies against creep corrosion

DfR Solutions (acquired by ANSYS Inc)

PNC Inc. Acquires New Horizontal Oxide Line

Industry News | 2014-12-12 12:24:17.0

PNC Inc. has obtained a new Horizontal Conveyorized CO-BRA BOND In-line Oxide Replacement line from IPS (Integrated Process Systems). The machine is capable of coating 100 panels per hour to help expedite the inner layer treatment process. Compared to the previous process of manual dip tanks, the Oxide Replacement line is far more efficient due to automation. By using fewer heaters, the new unit is more energy efficient as well.

PNC Inc.

Ultrathin Fluoropolymer Coatings to Mitigate Damage of Printed Circuit Boards Due to Environmental Exposure

Technical Library | 2016-05-19 16:03:37.0

As consumers become more reliant on their handheld electronic devices and take them into new environments, devices are increasingly exposed to situations that can cause failure. In response, the electronics industry is making these devices more resistant to environmental exposures. Printed circuit board assemblies, handheld devices and wearables can benefit from a protective conformal coating to minimize device failures by providing a barrier to environmental exposure and contamination. Traditional conformal coatings can be applied very thick and often require thermal or UV curing steps that add extra cost and processing time compared to alternative technologies. These coatings, due to their thickness, commonly require time and effort to mask connectors in order to permit electrical conductivity. Ultra-thin fluorochemical coatings, however, can provide excellent protection, are thin enough to not necessarily require component masking and do not necessarily require curing. In this work, ultra-thin fluoropolymer coatings were tested by internal and industry approved test methods, such as IEC (ingress protection), IPC (conformal coating qualification), and ASTM (flowers-of-sulfur exposure), to determine whether this level of protection and process ease was possible.

3M Company

Relative Humidity Dependence of Creep Corrosion on Organic-Acid Flux Soldered Printed Circuit Boards

Technical Library | 2018-05-09 22:15:29.0

Creep corrosion on printed circuit boards (PCBs) is the corrosion of copper metallization and the spreading of the copper corrosion products across the PCB surfaces to the extent that they may electrically short circuit neighboring features on the PCB. The iNEMI technical subcommittee on creep corrosion has developed a flowers-of-sulfur (FOS) based test that is sufficiently well developed for consideration as an industry standard qualification test for creep corrosion. This paper will address the important question of how relative humidity affects creep corrosion. A creep corrosion tendency that is inversely proportional to relative humidity may allow data center administrators to eliminate creep corrosion simply by controlling the relative humidity in the data center,thus, avoiding the high cost of gas-phase filtration of gaseous contamination. The creep corrosion relative humidity dependence will be studied using a modified version of the iNEMI FOS test chamber. The design modification allows the achievement of relative humidity as low as 15% in the presence of the chlorine-releasing bleach aqueous solution. The paper will report on the dependence of creep corrosion on humidity in the 15 to 80% relative humidity range by testing ENIG (gold on electroless nickel), ImAg (immersion silver) and OSP (organic surface preservative) finished PCBs, soldered with organic acid flux.

iNEMI (International Electronics Manufacturing Initiative)


sulfur searches for Companies, Equipment, Machines, Suppliers & Information

PCB Handling Machine with CE

High Resolution Fast Speed Industrial Cameras.
Electronics Equipment Consignment

High Throughput Reflow Oven
SMT feeders

World's Best Reflow Oven Customizable for Unique Applications
Global manufacturing solutions provider

Nozzles, Feeders, Spare Parts - Siemens, Fuji, Juki, Yamaha, etc...


Internet marketing services for manufacturing companies