I made my own wave measuring device using KIC2000 system. KIC2000 has automatic wave detection, so now I have a profiler for both reflow ovens and wave solder. The delmat carrier only cost $500. A guy, Samir, from this forum gave me the idea, actu
Electronics Forum | Mon Dec 17 19:01:45 EST 2007 | bbarton
As someone with a LOT of experience with the "low cost" alternative alloys, primarily SACX, I have one simple question....Are these shorts a new phenomena? WAS your process in control, and all of a sudden it's not? If the answer is YES, take a look a
Electronics Forum | Thu Nov 19 09:32:52 EST 1998 | Earl Moon
| | | | | | For some as yet unkown reason, we have started to have some boards sag and go under the wave. The boards are surface mount top side and conventional components wave soldered. We have checked the wave hight and both the profiles on the wav
Electronics Forum | Thu Nov 19 09:55:47 EST 1998 | Dave F
| | | | | | | For some as yet unkown reason, we have started to have some boards sag and go under the wave. The boards are surface mount top side and conventional components wave soldered. We have checked the wave hight and both the profiles on the w
Electronics Forum | Mon Mar 25 10:22:20 EDT 2013 | rgduval
You mentioned that you changed the layout some, and this can be essential in this type of process. If the SMT parts and TH leads have inadequate spacing on the bottom side, shorts may be inevitable (someone else will have to advise what the recommen
Electronics Forum | Fri Mar 22 12:11:56 EDT 2013 | emeto
Hi, I will focus on the flux one more time. Try different amount(usually more flux should give you better result). Also depends what kind of flux you are using? Water based or alchohol based? Try with another type that you are using. Check the spee
Electronics Forum | Fri Mar 22 10:33:58 EDT 2013 | mbrett73
Hello guys, I´m pretty new on pcba process and I´m writing to see if you can help me, we have combo process om pcb for UPS boards and we are facing a lot of shorts after wave the boards. We did few tests with different fluxes different profiles chan
Electronics Forum | Mon Jun 12 10:57:51 EDT 2000 | Jason
I am new to wave soldering. Any information is greatly welcomed. Here is the problem. After soldering the boards they have a film on the bottom of them and sometimes a white powder looking substance. I have tried decreasing the amount of flux on
Electronics Forum | Fri Jun 12 11:15:50 EDT 1998 | Ryan Jennens
Hey all! The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a pallet w
Electronics Forum | Wed May 21 09:31:09 EDT 2003 | caldon
I need to first understand what "Peeled the BGA off" means. Was heat used? was this the pry and lift method? We had shorts under some BGA's we have and the solder was bridging from lead to lead but not on the board level at the FR4 on the BGA creati