Electronics Forum | Tue May 19 13:29:33 EDT 2015 | dyoungquist
We have been running a Heller 1707EXL for 8 years and added a Heller 1707MKIII about 1 years ago. We have not had any problems with either one of them. We do both lead and lead-free assemblies along with BGA/LGA components. If speed/volume is not
Electronics Forum | Thu May 14 10:00:14 EDT 2015 | swag
I like MpM personally - run forever and programming is easy and leads you through it. It's hard to miss a step of programming with MpM software. DEK's a little harder (for me) but still very nice controls. The pluses of DEK - DEK has a high freque
Electronics Forum | Wed Jul 07 17:42:05 EDT 2004 | davef
Here's more on controlling the type of solder used in the assembly shop. http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=28859
Electronics Forum | Wed Mar 23 12:10:04 EST 2005 | dphilbrick
Has anyone out there done any lead free testing using a Vitronics Unitherm 500 oven? based on the specs I have dug up on the machine I suspect it should work fine but it would be great to hear from someone that has done it. Thanks in advance.
Electronics Forum | Tue Jan 31 13:41:12 EST 2006 | outgasser
We are currently experiencing problems with delamination during rework/2nd op activity on lead free. I am suspecting this is a result of the use of a heat gun to rework components. My assumption is that the high heat and time in area greatly increa
Electronics Forum | Mon Dec 22 10:43:18 EST 2008 | etechsupply
I wanted to hear from users of the SN100C alloy to find out what they think is positive and negative about this lead free alloy. Thanks, Keith
Electronics Forum | Thu May 22 12:32:35 EDT 2008 | tonyamenson
So here is my problem with the info you gave. If my preheat topside max is 150 - 170 C but my flux calls out a topside temp of 93 - 104 C..... ....Im pretty much up a creek becuase of a poor flux choice? FYI. we are using the Indium 3590-TX for bo
Electronics Forum | Wed Dec 22 12:36:36 EST 2004 | rlackey
Hi Mark, Look on the bright side, if you want to change from HASL you've got the lead free issue which will allow you to evaluate all other finishes, and find the best one for you. Dave, have you seen any unleaded HASL finishes & any issues arising
Electronics Forum | Tue Jul 13 06:49:53 EDT 2004 | imtiaz
In one board we are using 213 SMT components out of which 23 components are lead-free and the rest are leaded. The paste used is also leaded. Do we have to make any changes in the profile of our reflow oven ? Also will there be any negative effect on
Electronics Forum | Mon Dec 22 14:52:18 EST 2008 | wrongway
We run our process like that all the time paste then glue we use same profile as if we were just reflowing paste once in a while we have A plastic bodied part that has that problem we asume it was some mold relase still on the part basicly comtamena