Electronics Forum | Wed Jul 06 18:05:57 EDT 2005 | Dave
lead free transition. want to use lead free parts w/ lead solder.. any issues I should be aware of???
Electronics Forum | Wed Jul 06 18:11:37 EDT 2005 | russ
Please search the archives as this has been discussed on many occasions. Everything should be fine except for BGAs which will require a higher temp of 235C at the peak in reflow.
Electronics Forum | Wed Feb 16 12:34:49 EST 2005 | greg
Hi all We recently have a problem with component in package 0805 (capasitor 100nF). I have noticed that after reflow soldering only one lead of the component is soldered. The second one is just laying on the PCB land. We use screen printing process
Electronics Forum | Thu Feb 17 04:09:19 EST 2005 | greg
The solder adheres to the lands very well so i don't think that problem is with solderability of the PCB. Not wetting to the 0805 terminations. When the problem appeared with the 0805 we chenged the supplier. But there was commnon element Pb-free te
Electronics Forum | Fri Jun 23 15:11:11 EDT 2017 | emeto
Try add a pre-heater. If not change the process or the machine. With KISS you will hardly get any PCB to work properly.
Electronics Forum | Fri Sep 22 02:19:25 EDT 2006 | lead free tester
The directive is called RoHS. Meaning that is > not only the lead that is the issue. The > materials need to whithstand a hihger > temperature, not only delta T is an issue (but > huge). Moisture sensitive devices: how to handle > these? You wil
Electronics Forum | Sat Jun 24 07:23:06 EDT 2017 | tch
You will need to preheat the boards for a lead free selective solder process. A preheat module is critical for any wave or selective solder process, if you don't get the board preheated properly the solder is going to resist flowing to the top of the
Electronics Forum | Mon Aug 27 11:51:47 EDT 2012 | cobham1
Its no my turn to give some advise. My first question would be can you put the boards into a carrier of some sort. There are many wonderful companies that make carriers that are ment for running down a smt line. This can be expensive unless you order
Electronics Forum | Thu Jan 20 17:14:39 EST 2005 | jbrower
Today, I have just finished evaluating Kester's EM907 (SAC305)lead free solder paste and found that for our applications it performs as expected. End result that I am encouraged with the results that we got. The equipment that I used: An SMT2020 to
Electronics Forum | Thu Jul 20 16:04:22 EDT 2000 | Bob Willis
Tin/silver/copper is the alloy I have done most with and it would seem that it will be the alloy of choice if you look at the people doing the work. There are still some issues of fillet lifting which I have seen on PIHR soldering and the same in wav
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830