Electronics Forum | Tue Aug 30 15:29:17 EDT 2005 | pr
I agree with cmiller on almost everything except the fluxer. I have not found that to be the slowest part of the process. On a slightly populated board, preheat will be the biggest cycle time killer. On very highly populated boards, time spent at the
Electronics Forum | Mon Sep 05 05:47:32 EDT 2005 | stalkerb
We have found the service to be OK, however we are in Western Europe. We do have a local Agent for ERSA, and things were a little slow at first.........however we now deal directly with a contact in the Factory. This seems to work out well.
Electronics Forum | Thu Sep 15 06:59:33 EDT 2005 | Adam
Hi, No we did not look at Pillerhouse, We were not particular fond of "moving the product" principle to selective (i.e using a gripper over a static nozzle), as often this requires pallets, and our sister plant had already completed testing which a
Electronics Forum | Wed Feb 20 18:21:49 EST 2013 | caurbach
A question for all you wave experts out there: We run our wave with a constant flow over the back plate. I know it's recommended that we set the back plate so that the solder sits just at the top of the back plate with surface tension keeping it fr
Electronics Forum | Tue Jun 15 12:03:27 EDT 1999 | Dave F
| Has anyone had issues where bottomside double reflowed smt has fallen off in the wave when using voc-free flux? I have verified the hotter profile was not the issue by using an alcohol based flux with no problems.This voc-free flux is also not caus
Electronics Forum | Tue Jul 13 14:19:00 EDT 1999 | JohnW
| | | Hi, | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | | | | | | Sec
Electronics Forum | Tue Jul 13 14:25:57 EDT 1999 | Earl Moon
| | | | Hi, | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | | | | |
Electronics Forum | Wed Jul 14 21:34:16 EDT 1999 | karlin
| | | | | Hi, | | | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | |
Electronics Forum | Tue Aug 26 13:44:14 EDT 2008 | cgray
The chain and fingers for our Wave solder is getting a large amount of residue from the flux (high dissolved solids) we are using. Any recommendations for products that can clean polymerized flux.
Electronics Forum | Mon Mar 26 09:07:05 EST 2001 | T Gilmore
If you go to AGI's website, http://www.autogroup.com, go to products, wave pallets and materials used. You can view durastone propoerties and buy raw material from them. Let me know if you have any questions, Todd Gilmore President AGI