Electronics Forum | Mon Mar 26 09:07:42 EST 2001 | T Gilmore
If you go to AGI's website, http://www.autogroup.com, go to products, wave pallets and materials used. You can view durastone propoerties and buy raw material from them. Let me know if you have any questions, Todd Gilmore President AGI
Electronics Forum | Thu Apr 05 13:54:18 EDT 2001 | CAL
Do the parts sit directly on the PCB? Typical 2.0 mm Max is desired for the component to be off the PCB. Are stand-offs an option? The long lead wiggles as it passes through the wave and thus agitating the air out.Does your wave a "dancer" option?
Electronics Forum | Mon Jan 15 18:24:40 EST 2007 | greg york
probably volatiles in the joint outgassing as it comes over the wave, is the joint a yellowy colour as well, or any pictures we can view cheers greg
Electronics Forum | Thu Jul 15 14:38:38 EDT 1999 | JohnW
| | | | | | Hi, | | | | | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants)
Electronics Forum | Thu Sep 01 01:21:05 EDT 2005 | cmiller
PS, sorry for any confusion, ALDSMT and CMILLER are both me. ADLSMT is my user name on SMTNET and CMILLER is me, cmiller@adltech.com I usually use cmiler to reply to stuff as if anybody e-mails me it makes more sense. adltech.com is a work in progr
Electronics Forum | Fri Jul 08 09:57:31 EDT 2005 | fctassembly
Proy, Another issue is what exact formulation of SAC is used. Much of the SAC305 being used in Asia contains phosphorus, which is added in an attempt to reduce the heavy drossing that SAC305 produces. Phosphorus acts as a flux on steel so will increa
Electronics Forum | Thu Jun 30 18:40:06 EDT 2005 | KEN
What your asking has many variables. 1. Material: SS vs. Cast Iron. Iron is thicker. Which SS? 316, 316L 2. Pump speeds, turbulence, hours of operation directly affect equipment life. 3. Things like scraping the pots, the tunnels, impelle
Electronics Forum | Fri Jan 12 17:33:56 EST 2007 | John S.
I've not seen it on a solder joint, but I've seen it on an SMT pad that had been skipped in a wave solder operation. The boards were under inspection for poor solderability. We never really pinpointed the cause. It would make a perfect 6 pointed s
Electronics Forum | Tue Feb 07 09:49:10 EST 2006 | George
Hello everybody, I have been asked to establish a way to improve our wave solder process. I wonder where I should start. We collect data by inspecting our PCB's visually. What's the best way to report data? Ocurrence of defects in total among all
Electronics Forum | Tue Jun 04 09:46:54 EDT 2013 | markhoch
While both of those products do make it easier to profile the wave, a standard reflow oven profiler, with some long thermocouples, are all you really need. You can even use the standard Thermocouples and send the profiler through the oven on a traili