Electronics Forum | Fri Apr 18 10:45:34 EDT 2003 | tsongshe
I'm sure the parts and solder paste are well registered. these transistors are commonly to252 package,and sometimes to263 package.I 've a picture of these two diffrent kinds of pad patterns of to252,but i don't know how to post it here... Thanks ®ard
Electronics Forum | Mon May 05 11:35:00 EDT 2003 | Grant
Hi, This is an interesting point. I use Koki paste from Japan, and it's wonderful, however what properties of solder paste would make it "anti tombstone" paste? How does led free effect tomb-stoning? That would be interesting to know. We might go
Electronics Forum | Fri May 02 12:54:55 EDT 2003 | Chris Lampron
Hi LWEI, This is not a permanent fix for the problem. We have had similar experiences with double sided boards. As a fix, we have applied water soluble solder mask to the edges of the component. This holds the component adequately for second side pr
Electronics Forum | Tue Apr 29 07:12:49 EDT 2003 | Glen barden
Sn/Cu/Ni is introducted to me in wavesoldering lead free process. Around in our industry, we have a plenty of info. about SAC but not on this alloy. The distributor showed me some information about this alloy including less dross, more shiny /smoot
Electronics Forum | Thu May 01 18:37:31 EDT 2003 | gregoryyork
Did you get any dulling of the solder joints at all or importantly was the resist discoloured or bleached after cleaning. It is possible to absorb flux and saponifier into the resist and this will definately cause poor SIR or electromigration especia
Electronics Forum | Wed May 07 09:02:29 EDT 2003 | cyber_wolf
I was wondering if anyone has done a study on thermo couple attachment with light cure adhesive.I have read all the papers and articles about aluminum tape, Kapton, and high temp solder.I have yet to hear anything regarding the accuracy of light cure
Electronics Forum | Mon May 19 02:59:04 EDT 2003 | emeto
Hi, I can give you a few steps. 1. The solder paste. Take the profile that manifacturer gives for the paste. 2. Use termocouple to measure the tempereture. Put PCB and measure the temperature in equal terms. 3. Compare your profile to manifacturers
Electronics Forum | Fri Sep 12 22:57:13 EDT 2003 | Dean
What is the surface finish of the PCB? Tin? Imersion Silver? What flux is used in wave solder and / or SMT? I have much experience with silver migration and tin wiskers. Both can disappear during a reqork cycle. Both can be extremely difficult
Electronics Forum | Sat May 24 00:43:59 EDT 2003 | iman
Our engineers did a study on our medical product with 1mils standoff height, and one issue was 100% of the boards that underwent ultrasonic failed due to failure of the package wirebonding. Poor reflow control would be one area to review in any event
Electronics Forum | Tue Jun 03 06:29:43 EDT 2003 | mk
Orrrrrr, you could eliminate the printing, shorting, and special surface finishes by bringing the boards in with the paste already on them. There is a process that is a much more forgiving method for applying paste called solid solder deposit. Check