Electronics Forum | Fri Aug 18 11:01:52 EDT 2006 | Frank R.
Hi, We have two complete SMT line and in this department we use conveyors for board manipulation. Concerning the wave area we are not full efficiency and I have to look for conveyors and bar code reader to make board manipulation an automatic proces
Electronics Forum | Wed May 11 19:34:42 EDT 2005 | Tom B
You may want to check out Nihon Superior. Nihon licensed their Alloy to Aim for US production Late last month! The alloy uses nickel and the solder joints look amazing for "lead-free" they rival tin-lead in appearance. Other boasts is that you can
Electronics Forum | Fri Sep 08 11:38:42 EDT 2006 | GS
Last april,I have seen same behavior on a pot using SACX. Phenomena happened just few days after start up of a brand new solder wave. I know they have got the pot replaced but I do not know what about the new pot if had same problem. I know they mad
Electronics Forum | Thu Oct 24 10:05:59 EDT 2002 | Yannick
I don't know the name of the flux. but is a no-clean solder paste.
Electronics Forum | Fri Oct 25 05:43:14 EDT 2002 | hanvictor
i have the experience like that, it should have something to do with solder paste.
Electronics Forum | Wed Oct 28 09:37:32 EDT 2015 | capse
An alternative to selective soldering equipment is robotic soldering, like Japan UNIX.
Electronics Forum | Tue Sep 17 15:40:59 EDT 2013 | 18424
Good day all, I wanted to get a quick poll from the folks running SAC305 in their selective soldering equipment. How are final results? How repeatable is the process, any machine related failures? pumps? nozzles? etc... I am just looking to get a
Electronics Forum | Tue Sep 17 15:47:04 EDT 2013 | 18424
Good day all, I wanted to get a quick poll from the folks running SAC305 in their selective soldering equipment. How are final results? How repeatable is the process, any machine related failures? pumps? nozzles? etc... I am just looking to get a
Electronics Forum | Wed Jun 05 21:33:12 EDT 2002 | davef
Tough to say based on what you have told us. Things to Determine are: * Is the heat at the solder connections that are not reflowing properly adequate? * Is the pad surface of the solder connections that are not reflowing properly solderable?
Electronics Forum | Fri Jun 09 07:26:24 EDT 2006 | amol_kane
hi, gald to hear that yr process is working well.....we are in the process of buying a wave with SN100C solder.....any pitfalls/precautions that you took during the transition? did you do any DOE for setting up the profile values?? are you seeing a