Electronics Forum | Thu Apr 16 13:40:08 EDT 1998 | Chrys
| Is there anybody to help me ? | We have small balls appearing on the boards soldered by | wave soldering machine and it looks that use of nitrogen | is linked to the problem (because without nitrogen, we have no more | problems). | That remind you
Electronics Forum | Fri Mar 06 15:04:11 EST 1998 | Todd N
| We have a double sided pcb that is surface mount on both sides. Now a Through Hole connector has been added. Appart from hand soldering does anyone have info. on reflow soldering the part. The connector is 0.1mm pitch, square legs. | 1) Do you need
Electronics Forum | Fri Mar 06 23:02:43 EST 1998 | Scott McKee
| | We have a double sided pcb that is surface mount on both sides. Now a Through Hole connector has been added. Appart from hand soldering does anyone have info. on reflow soldering the part. The connector is 0.1mm pitch, square legs. | | 1) Do you
Electronics Forum | Mon Jan 26 11:46:16 EST 1998 | Rin Or
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Fri Sep 07 14:09:57 EDT 2001 | aqueous
Hi Carol, Pressure requirements have changed over the past few years. In the recent past, aqueous cleaning systems relied on high flow, low pressure �flooding� techniques. 20 � 30 PSI pumped through large orifice nozzles. With ever increasing boa
Electronics Forum | Thu Jan 02 12:15:10 EST 2003 | Mike Konrad
Richard, With respect to the Resistivity of Solvent Extract (ROSE) test, the test solution is exceptionally aggressive. With the Zero-Ion for example, the test solution�s resistivity is 150 M-Ohms. Additionally, because test solution is made up of
Electronics Forum | Tue Mar 04 17:27:07 EST 2003 | msivigny
Hello Dave, I can understand why you might not use the auto-correct function based on the time it takes to perform the operation. I question why there is an auto-correct function in the first place? If I understand the way this works correctly, the m
Electronics Forum | Tue Sep 21 11:39:41 EDT 2004 | pabloquintana
Conformal coat a bare board to determine if there > is there is enough surface free energy from your > solder mask to prevent dewetting. Sorry for my ignorance, but what is "enough surface free energy"? How do I determine that? >* Bake a board
Electronics Forum | Tue Sep 21 16:09:08 EDT 2004 | davef
Q1: What is "enough surface free energy"? A1: Look here for background: http://www.azom.com/details.asp?ArticleID=1575 Q2: How do I determine surface free energy? A2: We look at it a relative term. For instance, a semi matte finish on solder mask
Electronics Forum | Tue Dec 14 04:01:08 EST 2004 | paul_fisher
We have a problem with dendritic growth that is affecting a new board going into production. This is of concern because they were subjected to Damp Heat Cyclic Tests as part of the product validation testing during their development. Fails to date