Electronics Forum | Sat Aug 07 11:47:47 EDT 1999 | JohnW
| | | | | | | | | | | | Hello, | | | If you are using no-clean and they are entrapped in the flux it is also IPC accepted but i havent found a customer yet who agrees with that. Im sure you have checked your profile. I had the same problem with chi
Electronics Forum | Tue Jul 27 14:56:23 EDT 1999 | John Thorup
| | | | We are currently using a 65/35 solder for our wave process but are considering switching to a 63/37 for a substantial cost savings. No one here seems to know why we everused a 65/35 formulation in the first place. | | | | I understand 63/37 t
Electronics Forum | Tue Jul 27 17:23:45 EDT 1999 | M.L
| | | | Presently protos of micro-bgas (80i/o) pitch .030/.031 | | | | 12BGA per assembly | | | | | | | | The board is a (.062, 4 layers) FR-4 using Dry film | | | | Pads .014inch | | | | Vias within footprint .020inch | | | | Vias to be filled by b
Electronics Forum | Mon Jul 26 10:25:12 EDT 1999 | Boca
| | We are having a process related problem with pullup resistors on a controller card which has a I960 micro-processor. | | The controller monitors signal inputs and it's own resources then blinks a LED to indicate its working. The problem is that a
Electronics Forum | Mon Jul 26 14:14:51 EDT 1999 | Steve Gregory
| | | We are having a process related problem with pullup resistors on a controller card which has a I960 micro-processor. | | | The controller monitors signal inputs and it's own resources then blinks a LED to indicate its working. The problem is th
Electronics Forum | Mon Jun 28 11:47:54 EDT 1999 | Christopher Cross
| | | hello, | | | | | | has anyone tried dispensing solder paste in thru holes instead of waving or hand soldering. if so how did it work out for you. | | | thanks for the input | | | | | | wayne | | | | | | | | | | | We have tried this mainly
Electronics Forum | Wed Jun 02 23:53:09 EDT 1999 | Dean
| To you all for comment and summary, | | The following things I like without endorsing (PCB/PCBA stuff - outside the great women in my life [many] and without [mostly]): | | 1) A good set of design rules | 2) A good set of design rules meeting pro
Electronics Forum | Wed May 12 10:29:25 EDT 1999 | Timothy O'Neill
| | | Can anyone tell me what the recommended "typical" cooling rates are after reflow? Are the cooling rates considered as critical to control as the heating rates and why/why not? | | | I do not think there is a "typical" post reflow cooling rate
Electronics Forum | Tue Apr 20 22:09:03 EDT 1999 | Earl Moon
| | I am wondering if anyone has any info regarding solder paste misprint clean-up procedures for Entek Plus CU-106A PCB's utilizing a water-clean solder paste. In a implementation procedure they recommend a 2-3 minute wash cycle with the following
Electronics Forum | Tue Mar 16 05:11:47 EST 1999 | Charles Stringer
| | AVX and a few other companies make these chip transient voltage suppressors (TVS) parts that are a real *PAIN* to use. According to AVX: | | "Due to the semiconducting nature of the doped Zinc Oxide (ZnO) ceramic material, SMT TransGuard