Electronics Forum | Thu Jan 28 16:29:03 EST 1999 | Tom B
Okay, Another question, if the soldermask in not cured, then it is washed will water ingress (from wash or ambient ) play havoc with capacitance or dielectric of PCB. I mean will my crystal and clock circuits start "Y2K'n" on me. OR will my PCB go
Electronics Forum | Thu Jan 28 17:31:20 EST 1999 | Earl Moon
| | | Hello Netters, | | | | | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that t
Electronics Forum | Wed Oct 07 06:19:30 EDT 1998 | Charles Stringer
| | | Does sombbody know what DPM rate a good and reliable SMT assembly line (incl. solder paste print, assembly and feflow soldering) has? | | | DPM is Defects per million, usually measured on components. We run a process consisting of small to medi
Electronics Forum | Thu Oct 08 22:06:44 EDT 1998 | Eric R
| | | Does sombbody know what DPM rate a good and reliable SMT assembly line (incl. solder paste print, assembly and feflow soldering) has? | | | DPM is Defects per million, usually measured on components. We run a process consisting of small to medi
Electronics Forum | Fri May 29 16:07:55 EDT 1998 | Steve Gregory
| | Thanks Steve- | Here is the whole story: | | The solder balls are appearing all over, similar to a | splatter. They are relatively small. We are using H-Technologies | S-HQ no-clean solder paste. The stencil is 6 mil and the boards | are ru
Electronics Forum | Fri Aug 17 06:40:27 EDT 2001 | nifhail
Thanx Dave/Hussman.. We normally store our solder paste in the refrigerator at 0-10 Deg C as per what the supplier recommanded. Our floor temperature is controlled at 22 +/- 5 Deg C and Humidity is at 55 +/- 5%. Recently we have customer asking fo
Electronics Forum | Fri Jan 11 17:14:13 EST 2002 | davef
We have one product with electroless nickel, immersion silver solderability protection. We do not purport to be experts, but like many things, have seemingly boundless opinions. Side note: There are a least three different [maybe five] imm silver
Electronics Forum | Thu Apr 10 09:28:14 EDT 2003 | chrissieneale
Thanks for your replies guys, there's some good info there. Dave, answers to your questions: The stencil was initially a big problem as with the Egineering Model's (EM's) and Engineering Qualifing model (EQM's) we kept getting short circuits due to
Electronics Forum | Fri May 16 10:06:44 EDT 2003 | pjc
Traceability of raw material, personnel and equipment performance during product manufacture: Tracing raw material is done by recording the material mfg.�s batch-code that they assign during the material�s manufacture. This is everything from the fl
Electronics Forum | Tue Apr 24 09:12:07 EDT 2007 | patrickbruneel
I want to say one more thing on this; many times RoHS is compared to the CFC elimination. But there is a huge difference between the two for following reasons: In late 80�s scientific evidence became available that CFC�s contributed greatly to the o