Electronics Forum | Tue Dec 10 20:42:43 EST 2002 | davef
Vijay, Sounds like you're not spending enough time at liquidous plus 20*C. And you need to stay there for 5 to 10 seconds. I know, I know. We have used bucketsful of WS609 over the years. See, as you say, the melting point of your solder alloy
Electronics Forum | Wed Dec 18 15:00:17 EST 2002 | Chris Lampron
Good Day, We have been searching for ways to do this very thing. We have sent them out for cleaning in hot baths, ultrasonics, pressure wash, etc... The chains have come back cleaner than they left but not perfect. At one point, one of our engineers
Electronics Forum | Thu Dec 12 00:36:11 EST 2002 | Frank
We had one of these years ago. We had trouble with it recognizing fiducials consistently, but other than that it ran good. This assumes that the left head, which is mechanical centering, is working good. And I believe that the minimum component
Electronics Forum | Tue Feb 10 13:58:43 EST 2004 | EHess
Scott, We have 2 Amistar Placepro 5620's and 2 5720's. One with a TF-14. I've personally been working on these for the past 10 years or so. Have a pretty good grasp of the process, if placepro's are what you are using. Glad to see Amistar is
Electronics Forum | Wed Feb 11 13:42:11 EST 2004 | fatally_phoenix
Scott, We have 2 Amistar Placepro 5620's > and 2 5720's. One with a TF-14. I've personally > been working on these for the past 10 years or > so. Have a pretty good grasp of the process, if > placepro's are what you are using. Glad to se
Electronics Forum | Tue Dec 17 09:48:44 EST 2002 | russ
Temps are related to the components/PCBs being soldered. I am not aware of any Industry standard. If you are soldering flex circuits, .020" boards etc.. We use 500 deg tips a little thicker PCB/lead we go to 600, and so on. We never exceed 800 in a
Electronics Forum | Tue Dec 17 17:47:49 EST 2002 | Tim Marc
Dave, I�m talking about the 75% vertical fill of solder IPC 6.3 criteria (B), and 6.3.1 Fig 6-5. I also referred to the annular ring of the Plated-Through-Hole, being coated with solder mask. Semantics, yes I did refer to the Plated-Through-Hole (Sup
Electronics Forum | Thu Dec 19 12:08:01 EST 2002 | davef
Facts!!! I got facts. Mechanical strength experiments of Sn43/Pb43/Bi14: �Microstructural And Mechanical Characterization Of 43/43/14 Tin/Lead/Bismuth�; J. Marshall, J. Calderon, J. Sees; Soldering And Surface Mount Technology; 10/91, p25-27 Look
Electronics Forum | Tue Dec 31 01:58:19 EST 2002 | MA/NY DDave
Hi Sorry, even though I have seen a machine in action by a test engineering department years ago, and remember some advertisements since then, and maybe have seen one at a show, I don't remember the names of the companys. If I had to I could probab
Electronics Forum | Wed Jan 01 11:03:31 EST 2003 | davef
We just use stare titanium stiffeners from the wave soldering area. Titanium is probably over-kill for your needs, but will work. Sources for titanium stiffeners are: * APT 603.622.1211 Tom Dimagio * New Era Technology 603.669.77971 Jessie Ward * B
We are a global electronics manufacturing Solutions provider ....Our company supplies new and used SMT equipment, spare parts, consumibles, ESD supplies and services to a wide range of EMS companies.
Equipment Dealer / Broker / Auctions
Parque Industrial Nogales No. 5297 Zapopan
Jalisco, 14 Mexico
Phone: 523316044491