Electronics Forum | Mon Aug 19 11:36:27 EDT 2019 | bulur
How does no-clean flux residues on a PCB assembly impact the ROSE testing? Does no-clean flux residues on the PCBA dissolve in solution of ROSE tester and increase ionic contaminants level in terms of NaCl per surface area? Is ROSE tester solution (a
Electronics Forum | Mon Sep 12 22:50:52 EDT 2022 | superlen
Poly, I've seen the same error occur with our GI-14 when the glass scale encoder is simply dirty. If you bought the machines used, they could have been stored in fairly dirty environment. Just clean the glass scale. (use caution). We use lint free cl
Electronics Forum | Mon Jul 10 13:08:21 EDT 2023 | ttheis
Thanks, I do recall reading about loading firmware onto some of the VME cards (VRM axis controllers I believe.) I will review this again. I agree that it seems to be some issue with reading axis position after hitting the home switch. The first thin
Electronics Forum | Mon Jul 10 13:57:21 EDT 2023 | ttheis
We were able to get the machine to zero after 'scrubbing' the encoder head. We used a piece of paper towel and IPA and slipped it between the head and the scale. We moved it back and forth a few times to clean the head then blew out any remaining dus
Electronics Forum | Fri Dec 10 08:44:52 EST 1999 | Dave F
Vinesh: You�ll find no papers that "clearly describes the harmful effects" of your style "of white residues," because no one is crazy enough to brag that they are doing what your customer wants you to do. The residue of no-clean fluxes are designe
Electronics Forum | Tue Oct 13 18:28:51 EDT 1998 | Graham Naisbitt
Upinder, Using IPA does not cause the residue, it simply exposes it. Given that all fluxes leave reisdues, it follows that these MUST be benign - but how do you know, and how do you control it. You are using flux to remove oxides and give you a go
Electronics Forum | Mon Jan 27 12:02:00 EST 2003 | Mike Konrad
Dave is correct. No-clean flux + water = white residue (unless the proper chemical is mixed with the water). Additionally, no-clean flux + IPA = white residue. Many saponifiers work well as do other cleaning agents. White residue may also be a re
Electronics Forum | Tue Sep 21 16:09:08 EDT 2004 | davef
Q1: What is "enough surface free energy"? A1: Look here for background: http://www.azom.com/details.asp?ArticleID=1575 Q2: How do I determine surface free energy? A2: We look at it a relative term. For instance, a semi matte finish on solder mask
Electronics Forum | Tue Sep 11 22:52:18 EDT 2007 | davef
Here are some options for removing OSP coatings from pads of the BGA substrates. * Leave the substrates in storage for 13-14 months. Shelf life of OSP coating is ~12 months, depending on the product. * Wash the substrates in your aqueous washer. Ea
Electronics Forum | Fri Jun 23 14:10:01 EDT 2000 | Chrys Shea
Sounds like the mask to me. Had a similar situation a couple years ago. The mask wasn't fully cured, so it absorbed water that the preheaters couldn't dry out. When it outgassed at the wave, it caused a lot of micro turbulence that broke the surfa