| I am a printed circuit designer with a lot of mixed technology designs. I am searching for information on how to eliminate the wave solder step and reflow the the through hole components. If anyone has experience in reflowing smt and through hole
Electronics Forum | Tue Sep 01 16:52:45 EDT 1998 | Ryan Jennens
| I am a printed circuit designer with a lot of mixed technology designs. I am searching for information on how to eliminate the wave solder step and reflow the the through hole components. If anyone has experience in reflowing smt and through hole
Electronics Forum | Fri Sep 04 16:23:48 EDT 1998 | Dave F
| | I am a printed circuit designer with a lot of mixed technology designs. I am searching for information on how to eliminate the wave solder step and reflow the the through hole components. If anyone has experience in reflowing smt and through ho
Electronics Forum | Thu Aug 20 15:29:45 EDT 1998 | D. Lange
Re: Questions #2 Are you having solderability problems with that arrangement? Sounds like problems could be solved at the wave solder. If the customer has already spun pcb then sometimes for low volume it would be easier to correct the problem at wa
Electronics Forum | Thu Aug 06 03:57:59 EDT 1998 | STONEY TSAI
Hi, friends, The gold plating and HASL boards made some difference on solderability for both reflow and wave soldering processes. It is difficult to investigate the interactions between raw materials and process parameters setting. Anyone provides th
Electronics Forum | Mon Aug 03 13:51:41 EDT 1998 | Ted Nicholas
I am looking for some design guidelines (length, width, spacing) for solder thieves which are placed behind trailing pins of wave soldered SOICs. I'd appreciate it if some one could direct me to the appropropriate reference. Also, has any one perform
Electronics Forum | Wed Jul 29 13:44:45 EDT 1998 | David Spilker
We are investigating alternatives to HASL finishes for more dense PWBs. OSP is not a good choice because of low solid flux and possibly long shelf life. Immersion gold is expensive and so far has been more difficult to wave solder. Has anyone had
Electronics Forum | Thu Jul 16 14:29:00 EDT 1998 | Aric Parr
Contact me off-line. I inherited 4 of them. I cannot make recommendations in recorded media. However, yield is very good when PM is done properly. | Howdy, | Is anyone using Seho? Need to know more about 7000 series machines with nitrogen and ultraso
Electronics Forum | Wed Jul 15 05:36:34 EDT 1998 | Stoney Tsai
Bare board solderability plays a significant role of forming good solder joint. Currently, I can not find any information about bare board solderability testing procedure or methods. I think the procedure of testing should have some differentiations
Electronics Forum | Mon Jul 13 03:00:29 EDT 1998 | Bob Willis
Very good point. I will be linking back to the page shortly when the my 30 training videos, 15 CD ROMs are featured on the book store page. This will be happening shortly as its an administration thing. Thanks for the input there will be a wave solde