Electronics Forum | Fri Jun 12 14:31:04 EDT 1998 | Earl Moon
| | Hey all! | | The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a
Electronics Forum | Fri Jun 12 15:56:43 EDT 1998 | Ryan
| | | Hey all! | | | The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is o
Electronics Forum | Fri Jun 05 10:24:56 EDT 1998 | Earl Moon
| I have just been assigned to look into the ionic chromotograhy test on our PCBA but I have zero knowledge. Could anyone help to explain what is this test about? Is it | a) a destructive test? | b) What is the measurement unit of this test? | c) Wh
Electronics Forum | Tue May 19 08:48:05 EDT 1998 | Aric Parr
| | I am running boards with gold fingers on a pallet for | | masking purposes. The pallets worked fine for a while | | but know the gold fingers are getting solder on them. We | | have tried everythin: new pallets, cleaning the pallet | | and boa
Electronics Forum | Wed Apr 08 05:41:37 EDT 1998 | Alan Pestell
We currently use the Loctite system of Glue/stencils and are getting very good results. You may still have a height problem is you solder resist is too thick. The UK sales person is Bob.goss@loctite-europe.com & he may give you more help. The only ot
Electronics Forum | Wed Mar 11 11:05:06 EST 1998 | Earl Moon
| I am having a problem with Entek coated boards. The solder past seem to just ball up on the pads. I had no problems with the board when it was hot air leveled. The board is double sided surface mount. I have tried adjusting the oven profiles mak
Electronics Forum | Thu Aug 16 20:11:21 EDT 2001 | davef
Hussman is correct. Make those people quit. [Just walk-up, pimp slap 'em, grab their dental pick, and say "Dave says you can't use this any more. I'm just following orders."][Trust me, this is much smoother than the "Tonya Harding Approach" that I
Electronics Forum | Fri Aug 24 19:08:17 EDT 2001 | stefo
Happy Friday All! Well, it seems another "opportunity" has presented itself to me. Looking to assemble a 24" X 24", 52-layer board... piece-o-cake, right? Not real sure of all the components that are on it, but I do know that there is some 20-mil
Electronics Forum | Thu Aug 30 11:59:00 EDT 2001 | Spanky
Hey all, I have 3 questions about reflow. Hopefully someone can help me. 1. I am having a problem. I set the peak at 230 and my mole thermocouples are telling me the temp in that zone gets to 237. How is this possible even if the thermocouple
Electronics Forum | Tue Sep 18 12:05:08 EDT 2001 | jschake
Optimal Print Parameters: I have responded to a similar question in the thread titled �Stencil Printing For 0201 Applications�, posted by markt and will refer you to that for addressing this question. If you seek clarification on any of those point