Electronics Forum | Wed Jun 24 13:46:41 EDT 1998 | Chris Kelly
Brian, a couple of things really stick out here... 1) You are spraying what is referred to here at the CATT as "PINK DEATH" The 3355-11 is about the most active/aggressive flux you can get your hands on. I am concerned about both the condition
Electronics Forum | Thu May 28 09:23:59 EDT 1998 | Chrys
| Hello, | | I need some users information about "hot air knife" after the wave | bath: | - Defects reduction ? | - In what kind of boards(TH/SMT SOICS ect.) it is applied ? | - Where can I purchase it as a retrofit (Soltec Delta 6622cc) ? |
Electronics Forum | Wed Jul 03 11:37:36 EDT 2002 | fmonette
Dason, I apologize if some of the information sounds redundant but I don't think I explained my point very well (and the standard can get really confusing at times). I definitely agree with using C-SAM to look for internal defects. My only advise i
Electronics Forum | Mon Dec 11 20:44:37 EST 2006 | davef
Title : LEAD-FREE WAVE SOLDER FLUX EVALUATION Author : Michael Havener Author Company : Benchmark Electronics, Inc Date : 09/25/2005 Conference : SMTA International Abstract : The European Union�s deadline to ban lead in electronic pr
Electronics Forum | Fri Nov 05 10:35:18 EDT 2010 | methos1979
This was a great post from another thread here with some tips: Date: November 04, 2010 07:42 PM Author: eadthem Subject: Who has best desktop AOI ? We do almost exclusively SMT parts but for solder with a 45 degree fillet angle use vertical light
Electronics Forum | Thu Jan 20 13:21:54 EST 2011 | rgduval
Dean, In a previous life, boards came off of the machines, and went to SMT QC, then to SMT T/U before heading off to wash and through-hole. The concept being that the SMT "team" was responsible for the quality coming off the machine, with QC and T/
Electronics Forum | Fri Apr 29 14:16:16 EDT 2011 | ppcbs
Below is the long explanation. This defect is most commonly found with BGA components, but can arrise with all components. I see it happening more now with lead free boards that are being assembled with a no clean flux. Best short term remedy is t
Electronics Forum | Wed Feb 09 21:37:37 EST 2000 | Dave F
Rob: Someone's out there turning over stones, eh? Roller Tinning, Rolled Solder. In printed circuit fabrication, a surface coating of tin-lead, typically 1-2 microns thick, applied to preserve solderability. Still available from some fabricators
Electronics Forum | Fri Jan 05 12:01:26 EST 2001 | Jim M
I've been involved with no-clean flux and conformal coat in the past.It has been my experience that the amount of no-clean flux used is proportionate to how well the conformal coat adheres to the boards.No clean paste did not affect adhesion. The co
Electronics Forum | Sun Dec 03 15:35:44 EST 2000 | Michael Nguyen
Wow. And I thought I was the only one having problem with ceramic capacitors.I too am having problem with cracking ceramic capacitors 1206 package.We changed vendors and still having the same problem. I had to reverify my entire process and I had to