Electronics Forum | Mon Dec 17 19:18:53 EST 2007 | bbarton
OH MY GOD!! Finally it's becoming public knowledge here on the streets. YES germanium is in this material. As much as these guys and ALPHA METALS wanted to keep these things secret, anyone with a halfway competent lab would quicky find out why all of
Electronics Forum | Thu Dec 07 11:38:04 EST 2000 | Dason C
Please advsie what kind of the solder paste which you are using and we have experience when using Alpha WS609 and found a lot of foaming. Beside, are you using the spray fluxer for your wave or not? If you have spray fluxer then you don't need to u
Electronics Forum | Tue May 01 15:39:34 EDT 2001 | blnorman
Anybody else out there using LR-737? How is it packaged? We're using it in Semco cartridges which include a dasher and stir rod (used because the paste and flux separate relatively easily). If you are using it in this configuration, do you get a p
Electronics Forum | Sun Oct 17 09:27:58 EDT 1999 | Steve Restinetti (aka Bix)
Our SMT department uses Alpha Metals WS629 solder paste exclusively. Does anyone else use this paste and what do they think of it? I haven't evaluated other pastes yet and think that I'm sure there is something better out there. Feedback would be app
Electronics Forum | Thu Oct 07 17:05:38 EDT 1999 | Bix
I am thinking on testing or possibly changing my company's solder paste brand. Anyone have any suggestions or hints on how to cover all my bases before making such a bold move? Present paste used: Alpha WS-629 Paste to trial: Multicore OA Sys WS-22.
Electronics Forum | Mon Sep 20 14:53:24 EDT 1999 | Doug
I've had some trouble pasting a test board for a MicroBGA trial. Most of the paste remains in the stencil apertures. The stencil is 6 mil thick, laser cut and electo-polished. The apertures are 12 mil in diameter with 20 mil pitch. We are using Alpha
Electronics Forum | Fri Jun 25 09:43:24 EDT 1999 | Dave F
snip | | Dear John/Earl | | Thanks for your clarifications. To me also the problem does not seem to be linked with the PCB. The Pre heater temp. is set at | 450 degree C. We are using Alpha Aq. cleanable flux. Can you elaborate on the Desired
Electronics Forum | Fri Jun 18 15:30:38 EDT 1999 | M Cox
What's wrong with the Tin? Just wondering MDCox | | Electroless silver had promise, from Alpha, but I don't know where this ended up. Also Omikron's "white" electroless tin is proported to be a good alternative, though I've never been a big fan of
Electronics Forum | Tue Apr 06 13:11:22 EDT 1999 | Mike Konrad
I would recommend the following chemistries: Zestron Vigon SC200... Good but very $$$$ (703) 589-1198 Vertex (sold by Petrofirm and Alpha Metals)... Won't last as long as Zestron but must less $$$ (904) 261-8286 Kyzen... Also very good (800) 84
Electronics Forum | Mon Jan 18 21:34:02 EST 1999 | Kelvin Chow
| Hi, | I�m searching for manufactores of lead-free components (resistance, capacitors ...) | Do you know adresses, websides ... to get some information? | Please tell me. | Dear Marcus, You may contact Alpha guy to see if they will give you some i