Electronics Forum | Wed May 25 04:48:23 EDT 2005 | tomczyk
I have Siemens Sp-120 and there is HD deffect. Is there any way to start this line computer? Help!
Electronics Forum | Wed May 25 05:04:01 EDT 2005 | steve sennett
Fred, Yes it is along with a host of other parts for 180's and 120's including a vision system heads station comp.line comp. and cameras. you can reach me at ssennett@primus-tech.com
Electronics Forum | Thu Apr 21 16:27:33 EDT 2005 | Dave G
Look at your component datasheets. Most specify # of reflows & max temps. Most discretes are only rated for 2 or 3 reflows max. Why do you need so many reflow passes ? Dave G
Electronics Forum | Sat Apr 23 14:14:12 EDT 2005 | indy
i suggest not more than 3 too. if u r runnin more than 3, do electrical test..and look for visual changes Indy
Electronics Forum | Tue Apr 26 11:07:22 EDT 2005 | Mike G
Im guessing your using a PSA? We have had very little luck with this method of attachment as a standalone.Works great if you are using clips. I would suggest you look into a thermal adhesive.
Electronics Forum | Sat Apr 23 11:41:27 EDT 2005 | Dhanish
Biggest SMT issue we encounter in our production floor is Damaged Component,we have implemented a lot of action items but the reject is not declining.Can anyone suggest any special action taken to resolve this problem at your facility.
Electronics Forum | Sat Apr 23 19:40:25 EDT 2005 | molosse21
Give us more info on your pcb... Perhaps if you use a multi pannel pcb you can dammage components when its time to separate your boards.
Electronics Forum | Wed Apr 27 23:00:06 EDT 2005 | pdeuel
Definetly need more infomation. What kind of machine? What type of tool? Where in the process id damage noted, before or after reflow? What type of part? have you tried changing vendor?
Electronics Forum | Mon Apr 25 21:52:58 EDT 2005 | KEN
I wonder if yor customer means wrong "flux"? Your not solderng to gold. Your soldering to Nickle. The gold is disolved and dispersed. Your joint strength comes from the SnNi intermetalic.
Electronics Forum | Sat Apr 23 20:07:22 EDT 2005 | molosse21
Does someone use Ultrasonic washing machine to remove nc or rma flux residu from the pcb??? I have no experience with this device and I plan to use this for a very small production lot Do you recommand this ??? How are your results ??? What kind