Electronics Forum | Wed Sep 20 12:14:08 EDT 2006 | Rob
Good question - as it is a water based flux then you are going to get a very low level of solvent evaporation, and it's hardly going to be absorbing additional water whilst sitting around. (you actually want the water (carrier element) to evaporate).
Electronics Forum | Wed Sep 10 15:37:31 EDT 2008 | scottp
At the risk of painting with too broad a brush: QEs are like seagulls: fly in, make lots of noise, crap all over things, then fly away. Back to the knob turning vs. analysis debate. Part of it may be different industries. We're in the high reliab
Electronics Forum | Tue Feb 11 14:05:11 EST 2014 | dontfeedphils
I can't speak too much as to why your joints are appearing dull, even with the booster. I can recommend a new chemistry that Kyzen has out that I've been running for about a year now. Price is about the same, it can be run at low(er) concentrations
Electronics Forum | Wed Jan 15 10:31:55 EST 2020 | emeto
Having 10c thermal differential is a lot. Trying different paste might help - usually thermal expansion makes component detach from PCB, then joint is formed and solidified, then component goes back but is too late to form a joint. Cooling speed migh
Electronics Forum | Mon Jul 08 11:53:40 EDT 2002 | yngwie
Hi Guys, We prints solder paste on via hole as the holes are used as the test points. This is a clean process. In normal production, upon completion of a primary side, board will proceed to secondary process immediately. The problem happened when
Electronics Forum | Mon Nov 07 15:42:08 EST 2005 | chunks
Whoa! What the heck was that!? A commercial post?
Electronics Forum | Mon Nov 07 15:52:03 EST 2005 | Burgandy
Looks like a commercial to me....!
Electronics Forum | Tue Nov 28 09:37:39 EST 2006 | GS
Have you seen IPC-A-610 D ? regards GS
Electronics Forum | Tue Sep 09 07:42:25 EDT 2008 | wavemasterlarry
God..... give it a rest.
Electronics Forum | Tue Oct 21 13:53:36 EDT 2008 | ccouture
Could you elaborate a bit? What is tin phos additive?