Electronics Forum | Thu Nov 30 21:13:55 EST 2000 | Dave F
Can't find "WS601" on the Alpha site. What is that stuff? So, with nothing to go on, I'll just guess ... Yer probably cold welding the solder particles together. The nozzle size (inside diameter) determines the dot size. * With glue, small dot si
Electronics Forum | Wed Jan 30 17:48:31 EST 2002 | davef
Expanding on a previous poster's comments ... Vapor Phase Soldering. A solder reflow technology that uses a heated solvent to melt the solder. Buried deep in the recesses of the SMTnet Library is �Terms & Definitions�. We started using vapor phas
Electronics Forum | Thu Jul 31 23:52:12 EDT 2008 | roc2x
Hi, Im having problem on tombstone, The part is LF chip component 1005, and my solder paste is WS leded. tombstone is not in a deg angle but one side is soldered but the other side is just sitting on the solder. Looks like my solder can not wick up t
Electronics Forum | Thu Jul 31 23:57:11 EDT 2008 | roc2x
Hi, Im having problem on tombstone, The part is LF chip component 1005, and my solder paste is WS leded. tombstone is not in a deg angle but one side is soldered but the other side is just sitting on the solder. Looks like my solder can not wick up t
Electronics Forum | Tue May 28 09:08:52 EDT 2002 | pjc
Silkscreening is falling out of favor, as it should. SMT IC devices can have their "pin one" solder lands indicated by a round mark, like a fiducial or a "1" mark, both made from either the copper clad PWB material or silkscreened. I have seen some w
Electronics Forum | Fri Jan 24 22:50:51 EST 2003 | MA/NY DDave
Hi Again Distance is tough, besides far less exciting.. You got the panther at your breast, screaming!! Somehow you have to make this go the other way. Rather than solder flowing any old place it wants to, when it wants to. Chasing the heat, Chasi
Electronics Forum | Fri Oct 14 03:50:08 EDT 2005 | steve
Alot of folks are going to experience this with their poorly designed desoldering systems. I would check the temperature that is being delivered at the tip of the desolder gun. A small preheater is recommended. The other problem you will encounter is
Electronics Forum | Thu May 13 09:52:34 EDT 2021 | winston_one
Want to update this question a little, I know it appears few years ago, but I hope there is some updates... We have to assembly few samples of motherboards with this kind of finish (customer mistake during pcb order). Normally we can use leaded sold
Electronics Forum | Mon Nov 02 13:24:18 EST 1998 | Ryan Jennens
| Well my process is I'm running my belt speed at 3.50fpm and about 215 to 225 degrees top side. I got my main wave down to a little less than half the board thickness. I'm not using a hot air knife cause we thought it might create more of a problem
Electronics Forum | Thu Aug 13 07:53:40 EDT 1998 | Earl Moon
| | Couple of questions. | | 1) Are we talking alumina substrates as the ceramic material? | | 2) Are we co-firing gold as the conductors on the substrate surface? | | 3) In other words, is this a hybrid thick film circuit? | | 4) If so, how large or
.gif)