Electronics Forum | Wed Jun 24 16:23:29 EDT 1998 | Justin Medernach
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, Your concer
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Fri Jun 19 13:40:25 EDT 1998 | Terry Burnette
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike There has been a
Electronics Forum | Mon Mar 29 12:10:14 EDT 2010 | rway
Test Jet will work for catching lifted leads, certainly. X-ray is the only thing for testing for internal solder defects such as voids and cracks. I personally do not have any experience using X-ray, so I cannot advise on its reliability. Perhaps
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Fri Mar 24 12:16:37 EST 2006 | patrickbruneel
Darn Rob you're brilliant You just solved the dilemma of micro cracks and hot tear in lead free, just add a softer metal like.....and the joints won't crack. You wrote "BTW: Lead is far softer & dissolves far more easily than copper or tin, hence wh
Electronics Forum | Mon Oct 29 18:21:43 EST 2001 | slthomas
We recently have received a lot of warped (bowed and/or twisted behond IPC 600 specs.) bare boards (some our fabricator's fault, some ours by design) and I can't help but figure that long term reliability will suffer when building product with them.
Electronics Forum | Sat Oct 03 07:26:01 EDT 2009 | cflames17
Check the reference plate on the hydra to make sure it is not cracked or delaminated. I have had problems with the glue coming loose and the plate flapping causing this same problem. check hydra camera calibrations, this to may help.
Electronics Forum | Thu Mar 18 19:53:29 EDT 2021 | lhd_qa
Hello everyone. I am new to the forum so I am sorry if this has been asked before. Does anyone have any suggestions for counting partial reels and cut tape? We are a distributor and for our ecommerce PDC we keep having quantity issues. Currently, we