Electronics Forum | Tue Jul 20 14:17:34 EDT 1999 | Curtis
| We are a medium sized PCB assy. house manufacturing about 2000 motherboards a day. There is a major problem we are facing at the wave soldering stage, i.e. warpage of the PCB. As soon as the PCB touches the wave it warps severely from the centre
Electronics Forum | Tue Jan 14 11:39:51 EST 2020 | avillaro2020
Thanks Robl. I’ve contacted samtec followed their advice but ended up empty handed. Originally my stencil thickness is 6 mils, samtec stressed the need for the paste and charge to have good contact but this is challenged by the inherent charge non-co
Electronics Forum | Mon Jun 27 08:18:47 EDT 2022 | kelvinchoong
Hi All, Appreciate any inputs that may be given. Currently i am operating VP6000 Vapour Phase Reflow Oven from ASSCON. Over the last 2 years, we have around 100 different Recipes for many different PCBs. Each recipe is adjusted(6 Different Paramete
Electronics Forum | Mon Feb 21 11:22:21 EST 2000 | K. Ckak
Hi Kurt, I agree with Dave F. I had exact same problem with PBGA placement. We requested our PCB vendor to plug/tent via (button printing) after HASL with SR1000 which worked well in the long run. There are couple of failure modes associated wit
Electronics Forum | Mon Feb 21 11:22:21 EST 2000 | K. Ckak
Hi Kurt, I agree with Dave F. I had exact same problem with PBGA placement. We requested our PCB vendor to plug/tent via (button printing) after HASL with SR1000 which worked well in the long run. There are couple of failure modes associated wit
Electronics Forum | Mon Nov 28 09:46:24 EST 2005 | pjc
I have waved gold (ENIG) boards. That's a pretty hot pot at 260C, wow. I have used 245C with good results. All other parameters look OK a glance. Well, PCB temp looks a little hot too at 130C before pot. 90-100C is typical for most No-Clean flux. At
Electronics Forum | Fri Nov 08 14:45:12 EST 2019 | charliedci
Appreciate the input from everyone. The PCB is .062" thick. As a CM we are at the mercy of our customer at this point although (hopefully) they are receptive to advice on the next build. Titanium strips could be an option, I also thought there might
Electronics Forum | Sun Oct 11 13:53:26 EDT 1998 | Vincenzo Longobardo
I have datas to substain that a not wetting PCB ( the HAL oxided or not uniform in thickness )if soldered in reflow, it shows voids with X-Ray inspection.The voids are in side all the joints not only on the solder pads levell. Is there a technical d
Electronics Forum | Tue May 26 07:57:16 EDT 2009 | stevezeva
Grant, Look at Surface Mount Techniques: http://www.smtprinters.com/printers.html They make fully automatic printers that will print PCB's up to 30" X 60" and 1" thick. That's pretty large format if you ask me... Steve
Electronics Forum | Mon Jun 14 11:44:23 EDT 2004 | Dreamsniper
I have boards with bad HASL application. First they're not even. Second some pad edges have no HASL and still remains bare copper. What's the maximum and minimum HASL thickness required for a good solderability. My boards are about 6 weeks old, I kno
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830