Electronics Forum | Fri Aug 02 12:01:40 EDT 2002 | johnw
interesting, not at all what we were told so yes lot's of contradictions comming from them, I have to say personally I've not beein impressed with there technical service of late, are they getting complacent I ask? it's strange they say it'll cause
Electronics Forum | Fri Sep 07 04:25:52 EDT 2012 | grahamcooper22
As soon as the oven temp falls below 40 C and the RH rises above 5% then you need to consider that the floor clock will start. Long term storage of devices in an oven is not good for them as it reduced their solderability and can affect their perform
Electronics Forum | Wed Jan 17 21:40:49 EST 2007 | Sumbi
Oven keeps building up debri in cooling plates and flux system seems not very good. would preferr less maintance,no time. know of any work arounds.Oven is Paragon series.
Electronics Forum | Tue Feb 25 18:11:40 EST 2020 | kylehunter
> What we did not talk about is Mycronic machine. > Great choice for small batches. Yeah? That's what I keep hearing! Would use that exclusively for small runs, with the Opal for larger batches.
Electronics Forum | Tue Oct 21 18:30:30 EDT 2003 | russ
AXL, you could be right! I personally didn't switch they did it after i left. Is it possible that indium might have changed in the last couple of years? I remember Indiums specs stating 40% post residue? This was quite a bit higher than some othe
Electronics Forum | Tue Jul 30 08:40:43 EDT 2002 | pteerink
I have used both. The moles both do the same basic functions. Software options are a little different for each. If you're just looking for basic profiles/oven qualification, either will do a fine job. If you're wanting more in-depth details, I'd su
Electronics Forum | Tue Oct 14 23:40:36 EDT 2003 | Dean
Here is a tip. Do an evaluation on materials. DO not trust what anyone says about solder paste. There are just too may "experts" out there peddling the brand of the week. You can begin with the brands listed, but do your homework. You know your
Electronics Forum | Tue Feb 11 11:40:21 EST 2020 | emeto
Sebas, on your profile you have listed U2, U101, U102 and I was wondering if the questioned part is one of them. I attach a typical profile specs - you should follow the one for your paste. In the one you attached the slope is too fast, soak is prob
Electronics Forum | Mon Apr 14 20:13:40 EDT 2014 | davef
So, someone is going to get a chance to buy a nice and shiny oven, eh? Summary from my notes of old thread on SMTnet: Some people melt sugar and use that solution to clean cooked-on flux residue. Dissolve sugar into warm water, spray it on the area t
Electronics Forum | Thu Oct 31 13:46:40 EDT 2019 | johnce
Hello, I have searched the forums for this specific topic, but can not find the clarification I would like. I am setting up a baking system to "reset" SMD components using a vacuum-bake oven. According to the JEDEC-STD-033 standard, depending on th