Electronics Forum | Wed Oct 04 10:18:51 EDT 2006 | greg york
Now seen the Blow Holes and shallow inverted and non wetting problem an aweful lot over here. Over came the Blow Holes and shallow inverted joints by washing the bare PCB with hot Saponifier then rinse and dry = problem dissapears. Think most PCB ven
Electronics Forum | Tue Jun 13 12:00:15 EDT 2000 | Brian Larson
How long and at what temperature to you bake through-hole boards for moisture? I am getting blow holes after the wave solder. Everything points to the drilling of the board, but I need to prove that it is not moisture.
Electronics Forum | Tue Jun 21 14:27:14 EDT 2005 | Dreamsniper
Defects will result, Your cooling rate is affected because the hot air is not circulated properly. Outgassing will appear and you'll have pin holes / blow holes, disturbed joint etc. Correct me guys if i'm wrong. Thanks
Electronics Forum | Wed Apr 04 17:40:39 EDT 2007 | davef
Rob: How do you rework blow-holes and pin-holes? PTH plating thickness SB 1 thou or greater. Epoxy is hydroscopic. So, you should control the environment and/or bake the moisture from the boards before soldering. Search the fine SMTnet Archives f
Electronics Forum | Wed Sep 15 07:43:11 EDT 2004 | gregoryyork
It may be worth baking the boards for an hour at 120C and then trying it straight away do not leave them lying around.Is the fillet shallow and inverted back into the board. Do you have any blow holes as well? Cheers Greg BLT
Electronics Forum | Fri Sep 22 04:43:18 EDT 2006 | greg york
Interesting you should ask this what problems are you seeing. Non wetting and blow holes and shallow fillets at all??? Cheers Greg
Electronics Forum | Tue Aug 28 23:47:12 EDT 2007 | crashoveride
Blows holes are usually caused by improper amount of flux applied to the boards prior to WAVE process and, in some circumstances, can be related to the preheater settings.
Electronics Forum | Mon Nov 10 22:29:31 EST 2008 | fctassembly
Hello Hoss Voidin/blow holes can also be exacerbated by residual flux. Have you experimented with dwell times and separation speed parameters with your selective ? What related parameters are you currently running processing under ? regards Jim
Electronics Forum | Wed Jan 12 20:18:14 EST 2011 | Jacki
How many % were affected? If a few,it can be caused bcoz of PCB coating. We had encountered it and PCB house replaced for faulty boards. Since then, we do test first if we hve to solder PCBs from this PCB house.
Electronics Forum | Thu Jan 20 08:22:14 EST 2011 | padawanlinuxero
http://www.flickr.com/photos/94427924@N00/5372753378/sizes/m/in/photostream/