Electronics Forum | Tue Dec 10 10:26:56 EST 2002 | davef
Questions are: * What is the current plating on the connector that is over the "plating of the leads is Nickel (99.9% purity)"? * What are the temperatures and durations at those temperatures that you read on these connector leads? * What solder allo
Electronics Forum | Wed Feb 03 22:47:48 EST 1999 | Chris G.
| Hi! | | Does anyone know any roadmaps for board plating materials. Especially I'm interested in finishes, which are plated onto copper. | | Teemu M�kiniemi | Teemu, For some time now, as I am sure you are aware, the PCB industry has been tryi
Electronics Forum | Tue Jan 10 12:17:17 EST 2006 | Rob
Hi, The ROHS compliant parts are usually Matte Tin on the outer terminal plating. There are also 2 further types of metal on the average chip cap - the undercoat metal of the outer electrode & the inner electrode. These are usually the same & are
Electronics Forum | Sun Jul 29 08:36:39 EDT 2001 | davef
You have provided very little information. Two similar possibilites come to mind: poor pad solderability protection and old boards. POOR SOLDERABILITY PROTECTION: Maybe the nickel plating under the gold is oxidized, contaminated, or otherwise very
Electronics Forum | Mon Feb 27 09:09:36 EST 2006 | davef
Silver on your copper or brass part is a solderability protection. The silver diffuses into the solder and you solder to the base metal, either the copper or brass in your case. Soldering to copper is well known. The issues are soldering to brass
Electronics Forum | Tue Aug 31 12:42:45 EDT 1999 | Charles Barker
****************************************** ***************** HELP! *************** ****************************************** We are having a special ceramic smt board made. The boards are 16-up arrays that have smt pads on both sides. Only thre
Electronics Forum | Sun Apr 05 00:23:53 EDT 2020 | researchmfg
1. To protect the nickel and copper under gold plating from oxidization before soldering. Gold plating can extend the PCB self-life and improve the solderability for 2nd re-flow. 2. Provide a good bonding strength. For Chip on Board process that Gol
Electronics Forum | Tue Aug 10 09:26:49 EDT 2004 | davef
You should be able to solder to brass - check with you flux supplier to get their recommendations. The flux you are using may not have enough activation to breakdown the oxides on the brass surface. A word of caution - brass (copper and zinc alloy)
Electronics Forum | Fri Feb 28 11:02:06 EST 2020 | slthomas
I'm not 100% sure which type of gold you're asking about, but if you're talking about hard gold plating, I think the most common use is to provide a durable surface for things like membrane switch contacts because it resists abrasion and other mechan
Electronics Forum | Sun Dec 13 08:49:15 EST 1998 | Ron Costa
Has anyone had any experience with using this alternative plating process? Some board houses are pushing toward this plating. Is there any long term data on this process? Any problems experienced with smt and thru-hole? I've heard tin whiskers to be
.gif)
.gif)