Electronics Forum | Thu Aug 12 21:06:48 EDT 2010 | ptpaazmi
COLD SOLDER LOCATION U600/U601 Problem : Several XMp3i Rotary swithes were found to exibit intermittent function during a DV build at WNC
Electronics Forum | Mon Aug 27 11:51:47 EDT 2012 | cobham1
Its no my turn to give some advise. My first question would be can you put the boards into a carrier of some sort. There are many wonderful companies that make carriers that are ment for running down a smt line. This can be expensive unless you order
Electronics Forum | Mon Aug 27 12:31:04 EDT 2012 | rway
Its no my turn to give some advise. My first > question would be can you put the boards into a > carrier of some sort. There are many wonderful > companies that make carriers that are ment for > running down a smt line. This can be expensive > u
Electronics Forum | Wed Jul 15 10:25:26 EDT 2015 | shahrat
Hi brothers, Can anyone give me some clear ideas that which surface finishing is the best for PCBs used for LED TV motherboard production? Some says that OSP is good but it is not good for double sided board. So I am a bit confused in between HASL,O
Electronics Forum | Wed Jan 13 04:07:58 EST 2016 | crystalpcb
Hi Syed, I'm a PCB engineer from China. First:Immersion gold surface finish is the best for PCBs. Second:HASL(Lead-Free HASL) Then:HAL(with lead) The cheapest surface finish is OSP(After 15 days will be oxidized)
Electronics Forum | Fri Oct 16 07:24:09 EDT 1998 | Howard Eccles
With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to overcome
Electronics Forum | Sun Apr 24 09:12:00 EDT 2005 | davef
We're not sure what your customer is talking about either. Gold and tin form an intermetallic compound [IMC] that can cause poor solder connections. To minimize the potential of a problem, keep gold to less than 3 percent of the metal. [Search the
Electronics Forum | Fri Oct 16 14:36:11 EDT 1998 | Jeff Sanchez
| With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to overco
Electronics Forum | Fri Oct 16 21:17:04 EDT 1998 | Scott McKee
| | With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to over
Electronics Forum | Sun Apr 05 09:46:47 EDT 1998 | Earl Moon
| We are looking at reflow soldering some Flexi-rigid | pcbs. I have heard that IR reflow soldering can make the Polyimide "self heat" and cause de-lamination. | Does anyone have any info. The thermal problems associated with polyimide rigid/flex de
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830