Electronics Forum | Wed Feb 01 08:12:04 EST 2006 | Chunks
OK, this is easy. You say HIGH fall out, so I can assume 25 or 50%? If so, run 10 without the heat gun and 10 with. This should show you if the heat gun process is the cause or not. If the relay is a surface mount, hand solder them on. If it's a
Electronics Forum | Fri Apr 06 04:10:25 EDT 2001 | kensmoke
We recently had a multi block panal change at the vendor Now the production lines are producing solderability defects in great number. The makeup of the pcb is a type of fiber glass mask green in color and pads with no tinning just copper lands.
Electronics Forum | Thu Dec 05 11:36:30 EST 2002 | William Guatemala
Have you check the flux gravity lately? If not, Check the flux gravity every 6 hours to make sure proper parameters are meet. Here is a list of things that may cause your solder ball problems; Excecive heat, defective fixtures, preheating temperature
Electronics Forum | Mon Dec 16 19:05:57 EST 2002 | davidduke
Steve , I agree with all the responses you have received. Randy Villeneuve is absolutly correct in all of his assesments and I would consider him an expert with the process , Gris is correct about adding a "heat sink" to the process complicating pr
Electronics Forum | Wed Feb 16 14:47:04 EST 2005 | Valerie
Mike, To answer your question, Yes we have thru-hole parts on the boards that we converted to double-sided reflow, we use pallets to select solder the leads. I suppose Masking would work, but that's using a lot of mask. Can I ask, whats preventing
Electronics Forum | Mon Dec 18 14:36:09 EST 2006 | samir
Yikes!! In-line cleaning, to clean cosmetic and benign residues (from a NO-CLEAN) flux... You sure you can't switch fluxes? Another variable with residues is the solder mask. Depending on mask type (glossy, matte, semi-gloss, or semi-matte), will
Electronics Forum | Wed Feb 09 21:19:03 EST 2005 | Mrduckmann2000
Russ, We can not use a wave pallet, already went that route. We have parts next to the thru-hole pins and between thru-hole pins. I am going to try an experiment in the next day or so with solder mask. I plan to solder SMT parts on the back of se
Electronics Forum | Wed Dec 20 04:43:36 EST 2006 | greg york
Any decent flux would volatise off with the heat of the wave unless absorbed into the solder mask. Test this by trying to clean in alcohol or common solvent aerosol, if it does not clean then it is probably Mineral Salts from solder mask fillers. Ano
Electronics Forum | Wed Jun 28 16:16:09 EDT 2006 | Gman
Good article. Would EDX analysis of the cross-section at the void joints be a good method to determine any plating contamination or solder mask issues?
Electronics Forum | Mon Dec 18 23:24:50 EST 2006 | grantp
Hi, Yes, I would hate to resort to cleaning, but the product must be clean. We have been using palettes to keep most of the flux off the PCB, but there is still residue around the connectors. Does anyone suggest a good no clean flux to use with le
winsouce.jpg)