Electronics Forum | Wed Jun 29 17:18:41 EDT 2005 | GS*
Very interesting tread, many thanks to all. Matt please, now what does it mean for you? Will your custmer accept dull solder joints or will the plating be changed ? (ie. HASL, ENIG, etc) Tnks and regards GS*
Electronics Forum | Fri Jul 08 06:38:51 EDT 2005 | mattkehoe
I did not get that info. We sent them back and the vendor ran them through HASL finish. They processed very well after that. Thanks to everyone for the help. mk
Electronics Forum | Mon Jan 09 13:41:09 EST 2006 | slthomas
Take a look at the boards, too. Could the HASL be different (in particular a domed or convex cross section) than what you're used to seeing? Is your printer actually working properly?
Electronics Forum | Sat Jul 28 08:37:52 EDT 2007 | davef
There is no good choice. Board Finishes: Industrial/Battelle Class 3 Environment [Reliability Knowledge Gaps: For use of Pb-free solders in High Reliability Applications, J Smetana, iNEMI Availability of SnPb-Compatible BGAs Workshop, March 1, 2007,
Electronics Forum | Fri Sep 17 03:13:00 EDT 2010 | grahamcooper22
In HASL pcb coating you need to fully coat the pads with solder and then blow off any excess solder to leave a nice coating on each pad. Generally pcb manufacturers try to give you a flat pcb pad to make your solder paste printing more consistent. To
Electronics Forum | Fri Nov 16 03:38:03 EST 2018 | premkumar_haribabu
Hi all, We have to solder a nickel tabs ( coming in SMT reels ) in to HASL PCB finish pads using refow oven & during this we facing poor wetting issues, more voids & we done pull strenth , its came out with in 1 kg ,I doubt that nickel coated materi
Electronics Forum | Tue May 31 09:40:23 EDT 2005 | mattkehoe
We have some boards that exhibit poor solder wetting when reflowed. Nothing fancy, smallest pitch size .050. See photo's at http://www.sipad.net/SnPbwetting.htm Is this ; Contamination on the HASL finish? Insufficient solder,not enough to cover pad
Electronics Forum | Tue Jun 28 09:39:00 EDT 2005 | davef
Points to consider are: * Gold plating too thick [SB LT 8 uinches]. [Obviously, we're talking about actual plating thickness, not the specification.] * Reflow recipe improper [SB 220*C 5-10 sec]. A recipe that works fine for HASL needs to be hotter
Electronics Forum | Thu Apr 20 02:27:11 EDT 2017 | pavel_murtishev
Mile, Please tell me more about your soldering process: - Are soldering process parameters the same for all three pins? - Is unsoldered pin connected to thermal heavy copper polygon? - What is your board surface finish? HASL? - Sn/Pb or LF process?
Electronics Forum | Fri Dec 15 13:57:46 EST 2000 | genny
It is only after the reflow heating process that the peaks may show up, as the solder build up in some vias(due to HASL'ing) might drip down during reflow. I don't think I've ever heard of it being desirable to have a bare copper surface that will ox