Electronics Forum | Tue Jun 02 14:32:58 EDT 1998 | Chris Fontaine
We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not alwa
Electronics Forum | Wed Jun 03 01:06:13 EDT 1998 | Mike Moninger
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Tue Jun 02 15:53:32 EDT 1998 | Earl Moon
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Wed Apr 11 14:05:30 EDT 2001 | davef
No, there's not a really great epoxy product for attaching thermocouples in reflow. Specifically, what's your problem? From Sanders Temprobe verbage ... Adhesives There are two general classes of material commonly used to adhesive bond thermoc
Electronics Forum | Wed Jun 03 07:13:27 EDT 1998 | Tom Tellinghuisen
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Tue Jun 02 17:36:43 EDT 1998 | Chris Fontaine
| | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not
Electronics Forum | Sun Apr 25 04:12:34 EDT 1999 | Earl Moon
| At Sanders (Military manufacturer), we have only started using plastic parts within the past few years. After being tasked with reviewing the new J-Std-033, it became obvious to me our process for controlling device exposure is weak. We build very
Electronics Forum | Mon Apr 26 12:51:45 EDT 1999 | Bob
Steve, Moisture sensitivity needs to be taken seriously. Being in the commercial end of electronics now, I am using many plastic packages. Unfortunately, moisture sensitivity processing is not black and white and it does require procedures and dis
Electronics Forum | Wed Mar 24 08:48:47 EST 1999 | Dave F
| I WORK FOR A SMALL TO MID-SIZE CONTRACT ASSEMBLY HOUSE. WE ARE TRYING TO FIND ANY SURVEYS OR STUDIES DONE ON THE USE OF BGA'S BY COMPANIES ON NEW DESIGNS. THE WAY EVERYBODY'S ALWAYS TALKING ABOUT BGA'S YOU WOULD THINK THAT THERE WILL BE NOTHING E
Electronics Forum | Wed Jun 03 15:22:12 EDT 1998 | Greg Curler
| | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not