Electronics Forum | Thu Apr 15 14:09:48 EDT 2010 | richardli
We found stains on the boards come out of reflow oven. The board itself color changed to yellowish from white . We understand discolor soldermask due to high temperature. This can be acceptable by our customer not the stains. The stains look like wa
Electronics Forum | Mon Nov 05 00:51:58 EST 2007 | omidjuve
We have a problem with soldering of a 96 pin header connector(9001-11961c00l1a from kingmate) we use 3 different wave soldering but in all of the machines we have many short circuit between the pins . the wave soldering machines that we use is fr
Electronics Forum | Sat Dec 24 08:26:41 EST 2005 | GS
Thank you, very intersting. Seen they've experimented also Sn Cu Ni on wave solder. Rgards............GS
Electronics Forum | Wed Apr 23 17:28:46 EDT 2008 | davef
The need to prebake boards to remove moisture from the board [to prevent voiding] prior to wave soldering is driven by the thickness of through hole plating. * 1 thou [25um] or greater requires no prebaking * LT 1 thou [25um] requires prebaking
Electronics Forum | Fri Dec 16 08:00:26 EST 2005 | jax
What you are most likely dealing with: Insufficient Pure Sn layer ( multiple causes ) Because elevated temperatures accelerate the diffusion process, the thickness of the Pure Sn layer will reduce during every thermal cycle... ( bakeing PCBs, S
Electronics Forum | Mon Jan 31 12:24:24 EST 2000 | Dave F
Robert: Several points: 1 Dross is a mixture of various things with no "fixed" composition: � The obvious things are metal oxides mixed with metal and this can vary in color with temperature and composition - remember some intermetallic oxides form
Electronics Forum | Mon Aug 28 15:34:19 EDT 2000 | Steve Harshbarger
Hello Ramon, This is a very common problem that usually can be overcome. Can you tell me the flux type you are using (manufacturer, and flux number)? Has your board vendor, or type of PCB's changed (are they entec coated - bare copper)? What is t
Electronics Forum | Wed Aug 30 09:56:37 EDT 2000 | NLykus
Hi Ramon, We have had this problem before on our Seho Wave Solder Machine. We are currently using a spray fluxer as well. By imersing the PCB into the flux you stated you are getting good results. What you need to do is check your spray patter
Electronics Forum | Fri Apr 16 12:17:51 EDT 2010 | richardli
We have asked the supplier use whiter soldermask taking more heat. We also asked the board supplier to double coat board with soldermask. All these tries failed. We are wondering if the stains are flux contamination.
Electronics Forum | Fri Apr 16 14:01:48 EDT 2010 | richardli
It could be the flux condensed in the oven. We plan to clean the vent and filter next week. Then we see if help. I just want to see if anybody has same problem in experience. Soldermask supplier told us the same white soldermask always change to a l
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
winsouce.jpg)