Electronics Forum | Mon Oct 02 14:46:06 EDT 2023 | davef
Lab tests can confirm the composition of your material. I'm going with tin oxide. Tin oxide changes color depending on the thickness of the deposit. Your deposit is fairly thin. It will change to a brown color as the thickness increases. Your EDX
Electronics Forum | Mon Oct 02 13:04:54 EDT 2023 | proceng1
I did a post a while back about this with Selective. I don't recall all the details now, but you can search it.
Electronics Forum | Wed Sep 29 19:47:44 EDT 2021 | emeto
"For the lead free soldering of electronic assemblies, the inclusion of silver in the alloy results in better wetting compared to non-silver containing alloys and also allows for a broader process window. Silver also improves joint reliab
Electronics Forum | Mon Sep 25 15:32:21 EDT 2023 | joeljacobo
hello colleagues, Hoping that everyone is doing well, I am reaching out to you in the hope that your experience can help me. We have a wave solder with sac0307 alloy and the pot has turned a golden color, at first I thought it was common tin oxidat
Electronics Forum | Mon Dec 12 15:57:58 EST 2005 | Samir Nagaheenanajar
4% of the alloy), there is a ternerary phase (not sure if i spelled that right) where the melting point of the alloy is MUCH less than, say, SAC305's. Sn-Bi has also been associated with...... none other than Tin Whiskers. There are some in the in
Electronics Forum | Mon Dec 12 21:38:05 EST 2005 | davef
Effect of lead on bismuth solders * Lead from hot air leveling (HAL) coatings can diffuse through the grain boundaries of the alloy. * Lead can form a eutectic composition of Bi52Pb32Sn16 in the grain boundaries. * Melting point of this eutectic all
Electronics Forum | Tue Dec 13 14:55:12 EST 2005 | muse95
Your response is from the point of view of using a Bismuth solder with Pb plated leads. Samir's point of view is from Bismuth in the plating on the leads being used with a Pb solder. There is a very large difference in the amount of Bi that will en
Electronics Forum | Wed Nov 01 07:32:33 EST 2006 | davef
What you have run up against is the unfortunate consequence of the transition period from Sn-Pb to Pb-free. In the past 2-3 years there have been several studies highlighting the differences in reliability between mixed metal systems, Sn/Pb, and SAC
Electronics Forum | Tue Aug 22 16:02:07 EDT 2000 | Dr. Ning-Cheng Lee
If the thermal mass of the products is small, a tent-shaped profile is recommended, with peak temperature around 240C. The hottest spot on board should be less than 250C. However, if the thermal mass of the product is large, such as a large server PC
Electronics Forum | Tue Dec 15 14:38:23 EST 2020 | emeto
I have done it different ways on different equipment. 1. Remove alloy one from the machine. Add alloy two only. and use it.For next board, do the same. 2. There are machines with separate sections for PB and PC-Free, so pots are away from each other