Electronics Forum | Tue Aug 08 12:49:33 EDT 2023 | serge_pirog
I ask for advice on starting wave soldering machine. The soldering machine is not new. Are there guidelines for properly loading solder into a bath and more. I also ask you to recommend an alloy. What do you think about Alpha Sn Plus 07 or SN100C(Sn
Electronics Forum | Thu Jan 15 03:20:59 EST 2009 | sachu_70
Hi Andrzej, I guess you mean peelable solder resist. Good idea to try during R&D, but certainly not a solution on production floor. Also, few constraints to be considered such as presence of entrapped air between component and solder resist, the natu
Electronics Forum | Fri Dec 01 07:46:41 EST 2006 | davef
Bridging Causes: * Insufficient flux * Excessive pre-heat * High conveyor speed * Solder contamination
Electronics Forum | Wed Feb 12 20:13:39 EST 2003 | cmiller
Does anyone have any experience with setting up a nitrogen supply system to a wave solder machine that is equiped for it? Does the nitrogen need to be room temp or higher? Does it make a big difference with bridging or solder quality? We bought a use
Electronics Forum | Fri Feb 14 22:03:40 EST 2003 | caldon
Air liquide has some great articles on this www.airliquide.com Cal
Electronics Forum | Wed May 12 09:57:32 EDT 2004 | loz
Can you advise why the angle would need to be larger for LF process? Thanks loz
Electronics Forum | Mon Dec 04 21:36:13 EST 2006 | davef
For ppm data look here: http://www.ppm-monitoring.com/
Electronics Forum | Sat Aug 04 07:44:25 EDT 2007 | davef
Thermal cycle* * Requirements for and troubleshooting of poor barrel fill => Hole fill
Electronics Forum | Tue Aug 28 16:30:24 EDT 2007 | shrek
thats goofy
Electronics Forum | Mon Sep 10 15:30:29 EDT 2007 | davef
See there Mr. Smartbutt, you were correct in spite of your more cynical tendancies. B)