Electronics Forum | Sun Sep 29 13:04:58 EDT 2013 | KIC-Tech Service
Sr. Tech, As far as I’m aware, most if not all, manufactures of thermal profilers offer K type thermocouples as a standard for profiling in the electronics manufacturing industry. In my decades of experience in the reflow and wave solder industry, t
Electronics Forum | Thu Feb 02 12:39:41 EST 2017 | mnorthey
We have been using Vitronics for over 20 years with very few problems. I imagine Heller is just as good, I would rather you talk to your Solder provider Rep to find out about any add-ons you need for your specific processes. Along with that info and
Electronics Forum | Sat Mar 08 02:43:16 EST 2003 | Frank
We are trying to implement AOI into the mix. One PE wants it Pre-Reflow, to catch and fix the PnP screw ups and the other PE wants it Post-Reflow, because the oven will fix quite a bit of placement offsets and mainly to catch any problems that the R
Electronics Forum | Wed Jun 10 18:50:36 EDT 1998 | Earl Moon
| | | Does anyone have any info./studies on what the percentage or PPM defect rates are for each part of the typical SMT process. | | | Example: | | | Screen Print = 45% of total defects | | | Component Placement = 25% of total de
Electronics Forum | Tue Sep 22 09:59:15 EDT 1998 | Mike C
| Hi Jacqueline! | Do these joints that you're having problems with happen to be on fine pitch solder joints? Are the fillets staying attached to the foot and separating from the pads cleanly? | If that is true, are there many vias concentrated
Electronics Forum | Tue Apr 03 22:03:18 EDT 2001 | davef
With friends like you, who needs enemies? I�d guess that the perceived benefits of flat pads for your 20 mil pitch and below components counter-balance the higher cost, gold being a solder pot contaminant, limited solder mask compatibility, potentia
Electronics Forum | Mon Jul 27 03:20:42 EDT 1998 | Frank J. de Klein
Dear Dave, Sure we can ! There are two values going around. One is 50 mg/mm2 The other one is 30 g/inch2 (30 * 1000) / (25.4 * 25.4) = 46.5 mg/mm2 So we are talking the same language. Regards, Frank J. de Klein | | | Hi, | | | We have encountered one
Electronics Forum | Mon Jun 28 22:02:13 EDT 1999 | Dave F
| Hey there gang, how's it going ? | | Anyway's here's my probelm, got a new product to build double sided reflow, lot's of so20's and PLcc's 1206's, 0805's the usual stuff. Probelm is all the pad spacing of the 1206's are too big, my component's ar
Electronics Forum | Thu Mar 02 16:06:32 EST 2000 | eLDON sANDERS
Gentlemen, I too have been atacked by that "soldering to gold" and will add my 2 cents. I also had parts that would pop off the board when the fillet looked perfect. After lots of pain, experimentation, and sleepless nights, I solved it through a
Electronics Forum | Thu Mar 02 16:06:32 EST 2000 | eLDON sANDERS
Gentlemen, I too have been atacked by that "soldering to gold" and will add my 2 cents. I also had parts that would pop off the board when the fillet looked perfect. After lots of pain, experimentation, and sleepless nights, I solved it through a