Electronics Forum | Wed Mar 14 11:24:32 EDT 2007 | Scotceltic
Have you thought about switching to either automatic paste dispensers or rhemoetric pumpheads in order to contain the paste and only dispense what is needed during your shift ? I am not sure what type of printers you have, but I know both of these o
Electronics Forum | Tue Mar 06 09:42:15 EST 2007 | realchunks
Hi Mark, Solder paste will not flow on Ni like it appears on HASL. Where you print it is where it will reflow. Has been like that for years. As a CM you should re-engineer / recut your stencil to provide proper solder joints. I seriously doubt i
Electronics Forum | Wed Mar 07 16:14:24 EST 2007 | Mark
Hello, We replated the boards with new Ni and Au and the soldering flow is excellent. There is 100% covarage of the pad even for reduced appertures. Mark
Electronics Forum | Wed Mar 07 16:44:43 EST 2007 | realchunks
Well there ya go, this proves you can't engineer from your desk, thru a computer, miles away! I'm also surprised you answered back - most don't. Thanks Mark.
Electronics Forum | Sun Mar 11 19:48:17 EDT 2007 | abjason
There is nothing to argue if you had found Ni above or togather with Gold, definitly you got poor wetness and awful solderbility for sure.
Electronics Forum | Mon Mar 05 20:44:22 EST 2007 | Eric Lim
Hi, Can anybody tell me how to clear Fuji XP2 machine unused data. The machine will become very slow in loading data after long time used. Besides deleting program, what else the effective methods to solve this problem.
Electronics Forum | Tue Mar 06 08:03:23 EST 2007 | dscott
Try deleting the Production Data if you have not already tried that and do not need it..... Open the Production menu, click production data, select and delete.
Electronics Forum | Sat Mar 10 20:54:27 EST 2007 | Eric Lim
After tried your suggested method, the result stil same. The hard disc space can't increased, the processing still very slow. Can anybody who use Fuji XP machine provide more effective ways to help me solve this problem???
Electronics Forum | Sun Mar 18 00:13:57 EDT 2007 | ____
How many programs do you store at the machine? How long does it take to load a program, how many placements are in that program?
Electronics Forum | Wed Mar 07 14:19:04 EST 2007 | cyber_wolf
We use quite a few Invar stencils. I have several stencils that have apertures that fall below aspect ratio that work very well.