Electronics Forum | Mon Sep 24 16:04:48 EDT 2007 | flipit
I would look at SST International and Sikama International. You might solder using forming gas. Forming gas is 10% hydrogen and 90% nitrogen or 8% hydrogen and 92% nitrogen. Chris
Electronics Forum | Wed Sep 26 17:10:06 EDT 2007 | kgieskes
Universal has been producing Lightning pick and place heads for some years now. How are these heads performing these days? Speed, component range, reliability. Who has worked with them?
Electronics Forum | Thu Sep 27 13:09:12 EDT 2007 | Mag10
Does anyone have experience with DOE software? I see quite a number of them in the market like MiniTab, STATISTICA, Stat-Ease, etc... Which one would you recommend for Manufacturing process improvement study? Thanks for your feedback.
Electronics Forum | Tue Oct 02 15:33:28 EDT 2007 | shrek
So, a test probe from ICT will not make solder rust?
Electronics Forum | Tue Oct 09 14:10:52 EDT 2007 | hussman
What do you mean by "what do you mean"? I was just making fun. But if you want, you can take it the wrong way and blame me for everything.
Electronics Forum | Wed Oct 10 07:54:50 EDT 2007 | shrek
Hussman,I'm quite happy to exist alone in his swamp and dine on delicacies like pickled eyeballs. This means you, me lad. BACK OFF!
Electronics Forum | Wed Oct 10 08:51:29 EDT 2007 | wavemasterlarry
LISTEN our old Soltec never rusted so i don't know where all this nonsense with rust is going. Mika, how about that gobblett we were supposed to have together? ;-)
Electronics Forum | Thu Sep 27 15:26:57 EDT 2007 | ghenning
Can anyone recommend inexpensive testers for custom cable assemblies? I found a few from Adola, YPU, Cirrus, and Banair on Google. Your help is appreciated... George
Electronics Forum | Fri Sep 28 07:42:07 EDT 2007 | zanolli
We have the need to verify that proper intermetallic layer between a 100% Sn plated contact and the solder joint is being formed. Never having done this before: Is there any specifications, etc. that we can use as acceptability criteria?
Electronics Forum | Thu Oct 04 09:35:51 EDT 2007 | pbxtech
Thanks Jon! Good to know! I don't think my iron is ever set at 300*C, haha :), so mineral oil is probably not my best bet. I'll try getting some of that copper grease.