Electronics Forum | Tue Aug 07 20:43:47 EDT 2001 | davef
First, we know that MIL types are wont to use charts like that. Give �em Weibull distribution tables and then they�ll be happy, happy. A good book is Nelson �Accelerated Testing: Statistical Models �� Wiley Second, we don�t use that very nice stu
Electronics Forum | Wed Aug 08 21:18:15 EDT 2001 | davef
Get-out the razor blades, bud. You could run that sukka for 6 sec dwell, cook breakfast on it, and you still will not get fill. [Hole file that is, breakfast will go along ways if peckish, though.] You could fire-up the depleted ozone rework gun [
Electronics Forum | Fri Sep 14 15:31:02 EDT 2001 | davef
How in earthly heaven would someone else have a report analyzing the defects on your boards? Among the good failure analysis labs that can assess situations like yours are: * Robisan Laboratory 6502 East 21 St Indianapolis, IN 46219 317-353-6249 fax
Electronics Forum | Tue Jan 22 20:32:08 EST 2002 | davef
Oooo, thanks for the conversion. Being metrically challenged, az a skratchin ma haid thar fer a mite. We do a G-10 160 thou and have similar issues. Now, we�ve talked about barrel fill [ie, slowing belt speed, increasing pre-heat temps, etc] befor
Electronics Forum | Mon Feb 25 21:13:12 EST 2002 | davef
No, none of us can tell you what is the acceptable level of halide content or contamination in flux residue. The level of harmful residues on your product helps determine the reliability of your product. We know nothing of your product, its custome
Electronics Forum | Tue Sep 24 22:29:04 EDT 2002 | davef
First, I don't have a clear fix on the problem. Please drill-down to more detail. We appreciate that you probably don't know the parlance. Just describe what you have and then what you'd like to have. Second, most 0402 LED are fabricated just lik
Electronics Forum | Fri Oct 18 09:50:02 EDT 2002 | russ
Steve, I am not aware of any standards so to speak. But IPC 782 and 770 have some useful info regarding mounting and pad geometries for wave etc... Since I do not know what type of components you will be wave soldering I will just give you some
Electronics Forum | Fri Dec 13 10:23:55 EST 2002 | davef
Bright ideas??? Bright ideas!!! I got bright ideas. In order of decreasing luminosity: * Stop installing the socket, solder the PLCC to the board, dip the board. The socket is a waste of time and money. You never replace the PLCC in the field, a
Electronics Forum | Tue Feb 10 20:40:49 EST 2004 | Kevin McCarten
1st thing to be said; I work for a company that supplies Desiccant Dry cabinets to the electronics industry for the storage of moisture sensitive components. The answer here really lies in inventory management/control. Ultimately you want to avoid b
Electronics Forum | Fri Feb 20 12:55:43 EST 2004 | russ
Ah, the old contour wave. I don't really know how to adjust those to get correct backflow to reduce your solder volume. I need to ask why you are worried about this. Do you have a QC requirement in excess of IPC class3 wich allows for this joint t
IPC is the trade association for the printed wiring board and electronics assembly industries.