Pick and Place Camera sees Red

Electronics Forum | Thu Sep 08 09:41:51 EDT 2005 | PWH

If you do find your camera is bad, I think they are relatively easy to replace if you get a new one. I have done a 1.0 and 4.0 GSM camera replacements but not a PEC as of yet. If it's like the 1.0 and 2.6 and 4.0's, likely it is not tough but will

Fuji CP4&CP6 Placement issues

Electronics Forum | Mon Jan 30 03:42:49 EST 2006 | daxman

Thanks for the reply fellas, I spent all day today working on these machines, and indeed, this is bizzare. The main line was in production, and the placement was excellent on the CP6. I transferred a reel (400 parts per board) to the CP4 and the p

RoHS compliant PCB

Electronics Forum | Thu Feb 02 09:16:57 EST 2006 | lyrtech

Hi, I have some questions about material used in PCB for RoHS compliancy. It seems to be fuzzy between may manufacturer. Here are my questions: 1) What is the recommended material for lead-free assembly? 2) What's the difference between FR4 High Tg

Siemens Siplace S15 Operating

Electronics Forum | Mon Mar 06 13:00:37 EST 2006 | global

We have a Siplace S15 and I would like to know if it is possible to make it skip a part during the placement operation with out aborting the job? In section 5.4.4.4 of the user's manual it describes how to set a track to empty and proceed on with the

SUZUKI Pick and Place Machine

Electronics Forum | Thu Jun 01 07:40:23 EDT 2006 | netellink

I have a Suzuki vision machine with 4 heads (SMT-1000VL). This machine is using the camera to inspect the nozzels (4 sets) in the nozzel tray changer every time it is going to change the nozzel(s) in the 4 heads. The problem I have is now the machine

Printed Circuit Boards

Electronics Forum | Mon Oct 02 21:36:03 EDT 2006 | davef

All of us wave solder FR4 all day-long, not to say we have never had problems doing it. The selection of the laminate material should depend on the burnin application. We'd be concerned about a FR4 burnin board that saw GT 150*C for extended period

Type 3 vs. Type 4 solder paste

Electronics Forum | Fri Nov 10 09:13:34 EST 2006 | russ

Dave hit the cons pretty well for type 4 type 4 is used when you have extremely small apertures and type 3 will not fit into them or release adequately basically. I have not yet had application that requires it but got very close once, .007 circle

SMD flatness standard

Electronics Forum | Mon Nov 20 19:49:03 EST 2006 | davef

Sorry for stating this incorrectly. It should been: Bow & twist for bare boards and panels: IPC-A-610 Acceptability of Electronic Assemblies, 10.6: 1.5% for PTH only and 0.75% for SMT, acording to test method TM-650, method 2.4.22 IPC-6012, par. 3.

CP4 Placement/Pickup Height

Electronics Forum | Fri Feb 02 10:24:50 EST 2007 | FredC

Daxman, Have you eliminated nozzle variation? The difference between a new and used CP6 nozzle can be .15mm. On a CP4 I would think it could be more. On new Cp4 nozzles the difference in effective nozzle length should not be more than .04mm. You can

Pick & place

Electronics Forum | Tue Mar 27 19:58:13 EDT 2007 | colormaker

I have only used the Quad 4C, We bought it used and ran good right out of the box without the need for repairs. It uses quadaline and does not work very well on IC's. We place 30K 1206 parts a week with a 4 % dump to bin. I have to tolerance set to 3