Electronics Forum | Thu Oct 30 21:06:20 EDT 2008 | ashley
Hello mickd, For Fuji practice, the primary tooling hole preferably be 5mm from the edge of the PCB (lower right hand corner). This is the reference X0, Y0 co-ordinates in the Fuji program where placing co-ordinates going LEFT will be -ve value & go
Electronics Forum | Sat Dec 13 17:46:27 EST 2008 | ysutariya
If you're military then you're probably just needing standard 130Tg FR4 and tin-lead finish. I would check two things: 1. Bake temperature: Isola recommends 300F for 4 hours to drive moisture out. Lower baking temperatures do not require a linea
Electronics Forum | Fri Jan 16 16:36:37 EST 2009 | rwyman
We've used our standard chipbonder- Heraeus PD944- for this type of application. While it does cure before reflow, when the part is placed onto the site, the material compresses and spreads and thus that potential standoff isn't an issue. We've als
Electronics Forum | Tue Feb 03 16:42:50 EST 2009 | cuperpeter
Hello All, > > I have a problem with nonwetting Au > finish after second cycle of reflow soldering > doublesided boards. Solder nonwetted pcb pads (is > wicked to component terminations) Either these > pads or some of non component pads became
Electronics Forum | Fri Mar 06 12:23:39 EST 2009 | stepheniii
Are you working for an OEM? If so see if you can get your engineering department to change their "zero orientation" for the packages. At one place I believe the CAD department called them "G codes". What was really bad there was that one shape had
Electronics Forum | Fri Oct 01 00:49:33 EDT 2010 | darrenj
Yes, we have the Agilis stick feeder and it is a definite improvement on the vibe. It usually comes with a set of starter 'tubeforks', but i bought another starter set after a while since the individual tubeforks are relatively expenisive. Always g
Electronics Forum | Tue Apr 28 21:48:50 EDT 2009 | davef
Confirm the source of the issue. Run a coalescence test on both lots of paste. A simple coalescence test can quickly determine the condition of solder paste after prolonged use. Simply print a small disk [around 4-5mm diameter and 0.2mm thick - a bu
Electronics Forum | Mon May 04 14:24:12 EDT 2009 | jimmyboz
Ok, So, If all the servo amps on H1 remained on H1 and the amp you changed is on H2, I have to guess the shifting on H1 is unrelated to the servo prob. Is the shifting unsolderable? if it just looks bad but will reflow, it may have been occurring f
Electronics Forum | Wed Jun 03 16:26:37 EDT 2009 | wisch123
The most innovative new technology today is ccoming out of Fuji. They don't really advertise, so if you haven't gone to a show lately you might not have seen it. The machine is call the XPF-W and it sets the new standard for quality, accuracy, reliab
Electronics Forum | Mon May 25 08:37:28 EDT 2009 | d0min0
Hello, recently we changed supplier of the LF BGA, we did corossection and now have doubts... previous BGA specs : pitch 1mm, ball diameter 0.6mm future BGA specs : pitch 1mm, ball diameter 0.4mm on the crossecrion we found that one of the ball seem
IPC is the trade association for the printed wiring board and electronics assembly industries.
Training Provider / Events Organizer / Association / Non-Profit
3000 Lakeside Drive, 309 S
Bannockburn, IL USA
Phone: 847-615-7100