Electronics Forum | Fri Jun 08 08:26:14 EDT 2007 | davef
Testing for solder mask cure: Search the fine SMTnet Archives, for instance: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=15726 Residue after wave: Water in your wave soldering flux may cause your NC flux residue to go white. Indium W
Electronics Forum | Fri Oct 19 10:49:48 EDT 2007 | brulal1
Hi I will like to know what do you think about cleaning hand solder, my employee spend about 25% of they time to brush they hand solder with teddy pen cleaner, we used no clean solder wire. It�s not been the first time that I try to eliminate those c
Electronics Forum | Tue Mar 04 09:12:35 EST 2008 | davef
Q1. What would you recommend for the best practice or comparison? A1. We'd go with dip & look. It's easy and cheap, requires no advanced degrees in measurology. Have you reviewed "J-STD-002B - Solderability Tests for Component Leads, Terminations, Lu
Electronics Forum | Wed Sep 10 17:12:55 EDT 2008 | gregoryyork
I dont know about analysis on boards it is OK as long as the people carrying it out know how to interogate the answers.I worked on a problem just last week where an analysis house in China tested the resist then the pads and found on both surfaces C
Electronics Forum | Thu Nov 13 09:27:21 EST 2008 | cisridn
I have tried covering the vias with thermal tape and that did not work. I like the idea of plugging the via with a temporary solder mask. I will try that the next time I build a fixture which should be tomorrow. This is mainly a problem only becau
Electronics Forum | Thu Apr 09 00:35:06 EDT 2009 | padawanlinuxero
Hello! I am in a little problem, theres a problem in one of the components, is a new component that we are working with the leads are tin coated, and after we solder in the reflow oven, with lead solder, we took them to do a some test and on a cros
Electronics Forum | Fri Apr 16 11:36:33 EDT 2010 | fönsi
Thank you for the links. I didn't know that there are companys that build test systems for ultrasonic inspection. My idea was to use a ultrasonic detector similar to crack inspection, for example to detect if the cooling pad is melted, or a solder jo
Electronics Forum | Mon Sep 20 11:21:48 EDT 2010 | tony1
I have this NiPdAu small QFN packge sizes less than 2x2. I tried to do solderability Dip And Look test and there's always some units no wet on either ground pad and small I/O. Can someone help to explain why is this so difficult to set on this surfac
Electronics Forum | Wed Apr 27 08:19:41 EDT 2011 | charliedci
We are in the process of changing over our wave solder flux from alcohol based no clean to VOC free water based no clean. We are running an old Eletrovert with foam fluxer, tin lead solder. After preliminary testing on scrap boards and now starting t
Electronics Forum | Mon Apr 09 20:55:46 EDT 2012 | action_101
I forgot to add that we are using a 3 mil stencil. It seems like to me that may be there isn't enough flux left when we reach liquidous?? About half of the solder spheres do melt and wet on each pad, but the top half of each solder joint is just the