Electronics Forum | Mon Dec 06 10:32:35 EST 2021 | jineshjpr
Hi Everyone, Can you please suggest how to achieve 100% solder coverage of two Thermal pads on BRD1260C component..??? Surface finish is OSP Copper & Solder Paste is Sn/Pb 63/37. Component is Gullwing leads type. PCB having 1.60 mm Thickness.Peak Tem
Electronics Forum | Wed Dec 28 16:03:53 EST 2005 | Chris
I have lots of experience with thermosonic gold ball bonding. You can read the literature and you will probably find some papers that say you can do it. I have never been able to do it. We gold ball bond all day long with little problems at all bu
Electronics Forum | Sun Feb 04 15:06:20 EST 2007 | Scotty
Profile should have a longer cool soak. Verify as was mentioned all pin/fixture support through out the entire process. Print, Place, pre reflow hand load, post reflow, carriers, ICT, Depanel and FCT. Conformal Coated or Potted? Mylars work well for
Electronics Forum | Tue Feb 21 01:32:49 EST 2017 | soldertraining
Looking for advice on soldering lead free paste to a board with very heavy gold plating, In my opinion, Gold contact surfaces are often used on circuit boards with membrane switches which is a choice of technology for industrial, commercial and consu
Electronics Forum | Tue Nov 20 12:48:40 EST 2001 | tony_sauve
We recently experienced a problem w/voids (up to 65%) in uBGA solder joints. The only joints that have the problem correlated to pads which had blind 0.006" via's in them. The via's only extend down 2 layers, of the 18. 21 BGA's on the PCB, only expe
Electronics Forum | Thu Nov 22 12:56:12 EST 2001 | tony_sauve
Thanks for the comments & suggestions. Here's some info garnered from a telecon w/the PCB Fab house: -the blind via's extend from layer 2-17...this was a revelation. The info from our customer was that the via's only extended down 2 layers. Did I men
Electronics Forum | Tue Jun 08 17:12:42 EDT 2010 | flipit
Kic Thermal used Pyropel. Cut with a razor blade and glue together with a good Dow Corning high temperature silicone. You can buy Pyropel in various thicknesses. It is not cheap. $100.00 for a 24" X 24" X 3/16" sheet. You can buy at McMaster Car
Electronics Forum | Fri Aug 17 01:40:55 EDT 2001 | V.RAMANAND KINI
We are in the watch & clock Business. We have a Watch IC chip that has to be wirebonded using Ultrasonic aluminium wedge bonder. The wire dia is 1.25mil. The PCB is made of G10 Glass epoxy copper clad laminate. The copper thickness is 18 microns. The
Electronics Forum | Tue Sep 24 12:30:11 EDT 2002 | Claude_Couture
I'm just shooting ideas here, but maybe a via hole in the middle of the solder pad would drain the excess solder by capillary force? Or using a tin plated PCB and printing flux only, then place and reflow. depending on the thickness of the tin plati
Electronics Forum | Wed Jan 24 11:27:54 EST 2007 | bradlanger
We have been using SN100C lead free hasl for over a year now with good success. It is very solderable and has good shelf life. You do have to make sure the finish gets applied to the correct thickness. If the lead free hasl finish is not applied thic
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830