Electronics Forum | Wed Feb 25 16:39:29 EST 1998 | Eldon Sanders
I agree with Chrys, get the spike temp up and wetting is not a problem. However, when the palladium mixes in with the solder the joint will become more brittle. You need to make sure enough solder is printed on the board to minimize the concentrati
Electronics Forum | Tue Aug 07 08:20:47 EDT 2001 | CPI
Are there other components on the board? If so, how does solder quality look on them? Are they all reflowing? Are the sections of the uBGA�s sitting on a ground plane? Sounds like un-even heating. You should attach a couple thermal couples and see h
Electronics Forum | Thu Aug 23 21:00:10 EDT 2001 | davef
We do the same quadrent every four boards in placement inspection on a Orbotech.
Electronics Forum | Thu Aug 30 08:51:24 EDT 2001 | edmond
The bluetooth module is ROK 101 007. The board and the module cannot damage.
Electronics Forum | Tue Oct 16 17:32:04 EDT 2001 | scott
Anybody have any experience with SMT and PTH assembly on Teflon Bare Boards?
Electronics Forum | Tue Oct 30 21:42:32 EST 2001 | surachai
I have question about board baking after in line washing machine then I would like to know some information that ; 1) Do we need board baking after in line washing machine? Both bare board and assembly borad normally we don't bake . 2)In case of ne
Electronics Forum | Thu Nov 01 01:48:14 EST 2001 | hamos_wks
168hrs, 1week of storage and frequently applied for rework after testing.
Electronics Forum | Thu Nov 15 13:51:23 EST 2001 | jhingtgen
John, To answer your question, we have a number of customers that are using this process, Pumpprinting very successfully! If you would like to contact myself I can provide you with some very good references that will be able to answer all your ques
Electronics Forum | Fri Nov 16 06:06:59 EST 2001 | genglish
John where in the world are you based?
Electronics Forum | Fri Nov 30 15:27:19 EST 2001 | Rex Gustafson
Where can I find pcb scoring guidelines for boards with different thicknesses, panel arrays, ....?