Electronics Forum | Thu Aug 27 13:14:49 EDT 2009 | ghepo
I have already told you that is not possible solve this problem by e-mail, without perform a detailed failure analysis. Also I have told you to procede by exclusion. Are you sure, by tests, regarding the PCB quality ? Are you sure regarding the solde
Electronics Forum | Thu Jul 08 09:29:10 EDT 2010 | mb_mfg
There are several things that can be done. Shortening the lead length should eliminate bridging between lead. We had done a project several years ago where the customer had shortened the leads to almost flush to the board, preventing any chance of
Electronics Forum | Wed Dec 04 04:28:58 EST 2019 | oxygensmd
It seems there isn't right connection between solder and solder-legs. Maybe check that the LEDs get huminidity, have some oxidation on the legs, try different solder paste, check the reflow solder profile. On the photo I can not saw properly reflowe
Electronics Forum | Thu Dec 05 05:39:05 EST 2019 | oxygensmd
I know your application isn't BGA but the data sheet also mention about the peak temperature - 235 Celsius. For the LEDs you can reach higher temperature and I recommend to reach 225-235 Celsius. You will get significantly better results because the
Electronics Forum | Wed Dec 11 06:47:33 EST 2019 | ameenullakhan
Dear Friends, Need your valuable feedback on how to identify the component is ok or not for manufacturing. Issue : We have parts which are more than 5 years old.And management want us to qualify this parts for production. We presently use below me
Electronics Forum | Fri May 29 17:07:00 EDT 1998 | Dave F
| | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localized
Electronics Forum | Mon Feb 12 10:02:18 EST 2007 | rgduval
A little late to the party here, sorry... Has the joint been verified as a cold solder joint? That is, visually confirmed that it looks like cold solder, and, perhaps, xrayed to confirm the solder status? X-raying may sound a bit extreme, but you'
Electronics Forum | Wed Sep 05 08:50:04 EDT 2001 | davef
No arument with others comments about moisture, but taking a different tact, consider that the volitle elements of the solder paste disppear as a function of the amount of time the paste is out of the container. [Maybe as a function of solder paste
Electronics Forum | Thu Sep 26 20:43:51 EDT 2002 | davef
"OK. If the connection doesn't look like I expect it to look, how do I know that the metallurgy is correct?" Comments are: * There are no pictures that will get you though this. * You should expect that gold that is dissolved in Pb/Sn solder to make
Electronics Forum | Fri Jul 30 17:26:02 EDT 1999 | John Thorup
| | Surface Mount Components like QFP's in Tray usually comes sealed in an anti-static plastic pack. In case the QFP's were removed from the said anti-static bag for more than 2 weeks, do these components needed to be baked for they might produce so