Electronics Forum | Tue Jul 06 16:59:36 EDT 2004 | davef
I'm sorry for not being clear. The "1 thou" refers to the thickness of copper that rides below your ENIG. If your HIC card is blue that's good. If it's some other color that makes you nervous, then you make of it what you will. They're pretty muc
Electronics Forum | Mon Jul 26 06:32:58 EDT 2004 | cyber_wolf
Grant, The only thing that you really gain from refrigeration is a couple more months� shelf life. Refrigeration also seems to slow down flux separation. I am not sure how your paste consumption is, but we use ours up way before the expiration date
Electronics Forum | Wed Dec 15 21:29:34 EST 2004 | davef
We�d say that it�s incorrect that ENIG solderability protection cannot be steam aged. It�s true the immersion tin and silver cannot be steam aged. We believe that most of the issues surrounding the poor performance of ENIG after steam aging is attr
Electronics Forum | Sat Feb 26 22:32:42 EST 2005 | siverts
The directive is called RoHS. Meaning that is not only the lead that is the issue. The materials need to whithstand a hihger temperature, not only delta T is an issue (but huge). Moisture sensitive devices: how to handle these? You will see an increa
Electronics Forum | Fri Sep 22 02:19:25 EDT 2006 | lead free tester
The directive is called RoHS. Meaning that is > not only the lead that is the issue. The > materials need to whithstand a hihger > temperature, not only delta T is an issue (but > huge). Moisture sensitive devices: how to handle > these? You wil
Electronics Forum | Wed Feb 16 12:34:49 EST 2005 | greg
Hi all We recently have a problem with component in package 0805 (capasitor 100nF). I have noticed that after reflow soldering only one lead of the component is soldered. The second one is just laying on the PCB land. We use screen printing process
Electronics Forum | Thu Mar 24 07:06:06 EST 2005 | davef
There's a lot of comparison tables on the web. Here's one: Properties - Summary [A Winlow Circatex] Attribute||Hasl||Immersion Silver||Immersion Tin||Electroless Pd||OSP||Eless Ni / Imm Au Shelf Life (months)||12||12||12||12||12||6 Multiple Reflows
Electronics Forum | Mon Apr 18 12:28:33 EDT 2005 | davef
We've never heard of it either. Stained glass widow people use varous types of copper and brass tape / foil in their work. A widely used suppler of this tape is Venture [ http://www.venturetape.com ]. They may be able to help. We're not sure how
Electronics Forum | Thu Jul 28 09:47:06 EDT 2005 | fctassembly
Hello Carl, The main reason there is little information on lead free soldering to ENIG is because most of the lead free soldering to date has been Japanese consumer products. To keep costs down, the major surface coating used has been OSP copper. It
Electronics Forum | Mon Aug 01 18:50:46 EDT 2005 | crishan
Hi Cecil, We using conformal coating in our manufacturing area, we did use to use Humiseal, others have been Bectron and Peters. We recentalt switched all lacquering to Peters, since it is lead free and it is a lot friendly than Humiseal. To answer